At present, the common air ducts in the domestic market are generally made of galvanized iron sheet, commonly known as white iron sheet. wear-resisting rubber liner And the thickness is 0.44~1.22mm. The thickness of iron sheet of air duct in China is generally less than 1.5mm, and the thickness of zinc coating refers to the national standard GB/T 13912-2002: 35 μ m. Average 45 μ m。 During the production of galvanized air duct, the national standard requires us to understand the following figures: 1. Appearance: conduct appearance inspection on all hot galvanized parts, and the main surface should be smooth, free of falling off, roughness and zinc spikes (if these zinc spikes will cause damage), free of peeling, missing plating, and residual solvent residue, There shall be no zinc lump and zinc ash in the parts where hot galvanized workpieces are used or where they are corrosion resistant. Note: "Roughness" and "smoothness" are relative concepts, and the coating roughness of workpiece is different from that of mechanical roller or (and) blow molding and galvanized products (such as galvanized steel plate and galvanized steel wire). As long as the coating thickness is greater than the specified value, there may be dark or light gray uneven areas on the surface of the plated parts. White rust (mainly white or gray corrosion products of alkaline zinc oxide) is allowed on the surface of galvanized workpieces stored in wet conditions. 2. Thickness: quantitative sampling shall be carried out according to the specified test method for coating thickness test. According to the size of the main surface area of hot-dip galvanized parts, the coating thickness measured in the test shall meet the following requirements: A) For parts with the main surface area greater than 2m (i.e. large parts), the average coating thickness measured on all basic measured surfaces of each part in the sample shall not be less than the minimum value of the corresponding average coating thickness: B) For parts with the main surface area less than 2m, rubber liner Price The local coating thickness measured on each basic measuring surface shall not be less than the minimum local thickness, and the average coating thickness measured on all basic measuring surfaces of the sample shall not be less than the corresponding minimum average thickness.

wear-resisting rubber liner The inner and outer walls are smooth, the resistance of the air duct is small, the secondary noise is not generated during air supply and exhaust, the energy consumption is reduced, and the operation cost is saved. The product can be made on site, cut, drilled, and opened, the installation is simple, and the labor and time are saved. The user's investment cost is reduced, the construction period is shortened, the performance price ratio is high, and it is cheaper than other materials. After the installation is completed, no maintenance is required, and the maintenance cost is reduced. The key points of whether galvanized sheet air duct material galvanized sheet is corroded are mainly reflected in the following three aspects: ① The first corrosion of galvanized sheet in the entire service life cycle is the oxidation of the galvanized layer on the surface, resulting in white rust. After a little longer time, the white rust on the surface further reacts with carbon dioxide and other impurities in the humid air to form black spots. When the galvanized sheet is used for a long time and the galvanized layer is severely corroded, the steel base loses the sacrificial anti-corrosion effect of zinc, and begins to oxidize to generate red rust. Once the steel base begins to oxidize, the corrosion rate becomes very fast, and the life of galvanized sheet ends. ② In addition, there are two special corrosion conditions of galvanized sheet, namely, black stain. One is that after being used for a period of time, due to the influence of lead and other elements in the zinc coating, the galvanized sheet will become black in the matte part of the zinc flake. The blackened zinc coating still has a protective effect on the steel base, but has a certain impact on the service life. ③ rubber liner Price It has excellent corrosion resistance in dry or pollution-free environment. However, in the polluted environment, the service life will be greatly shortened, so it is necessary to pre coat the film into color plates before use.

wear-resisting rubber liner It will burst for a long time due to frequent and severe pressure shocks. This situation is usually not caused by excessive static pressure, but is related to the strength and frequency of pressure shock. During the operation of construction machinery, the oil pressure in the oil resistant hose will rise or fall repeatedly, and then it will form frequent pressure shocks to the oil pipe, causing the oil seal of each part to become more damaged, the oil resistant hose will bubble and break, and the pipe joint will become loose and leak. Therefore, in the process of operation, the valve rod should not be pulled too hard, and it needs to be gentle. The application temperature of the oil in the oil resistant rubber hose is too high, resulting in aging and bursting of the rubber hose. During the operation of construction machinery, the hydraulic system will cause the oil to become hot due to power failure, and the influence of external temperature (especially in summer) will cause the oil temperature to rise sharply. The higher the oiling temperature is, the easier the rubber hose ages, the worse the elasticity is, the lower the strength and sealing function are, and the oil resistant hose will burst quickly. Therefore, rubber liner Price During operation, when the temperature rise of the hydraulic system is too high or too fast, the causes should be found and eliminated in time. Necessary cooling measures shall be taken for summer operation, especially continuous operation.

“ wear-resisting rubber liner What are the applications in engineering transformation? " In this issue, we will explain this problem for you. Those who have consulted this problem will come to see it: First, we should consider the water supply and drainage of all water related equipment, such as wells, pumps, etc., their location, installation method and temperature, including galvanized air ducts. 2、 It is very important to consider galvanized air duct in advance to avoid temporary replacement of galvanized air duct materials. 3、 After the location of the machine tool is determined, the drainage outlet can be considered to be arranged underground, which is not only convenient but also durable. 4、 After river reconstruction, there should be a suppression test, but now many construction teams do not suppress the test. It is usually said that it is not important, that there is water and pressure in the galvanized air duct, and so on. Try to be present to suppress the test. 5. If the installation is completed, pay attention to the inspection of the workshop, water pump room and FRPP drain. If the drainage system is slow, the installation program should be able to open the installation. Water outlets should be protected, especially during civil engineering construction, rubber liner Price It may cause soil loss and blockage. I believe that you have a better understanding of this information, and we will continue to improve the galvanized air duct to make it more widely used.