Changzhou Acetylene pipe With the continuous updating of technology, the products are also developing in the continuous updating. At present, the inspection requirements of rubber hose are also improved compared with the previous ones. The inspection index of ultra-high pressure hose shall meet the following index requirements according to the requirements of the Safety Code for High Pressure Water Jet Cleaning Operation: 1) The bursting pressure shall be more than 2.5 times of the working pressure. 2) The test pressure shall be 1.5 times of the working pressure, and the pressure shall be kept for more than 2 minutes without damage. 3) Pulse pressure shall be within the range from zero to working pressure, and 50000 pressure pulses shall be free of damage; The pulse frequency is 15 times/min when the working pressure is 1000-2800bar, and 110 times/min when the pressure is above 2800bar. Since high-pressure cleaning machine has been widely used in all walks of life, and the working condition of high-pressure hose is relatively the worst, we must pay attention to the quality when selecting high-pressure hose, so as to avoid unnecessary safety accidents. Acetylene pipe Price The development of rubber hose can not be separated from cooperation, R&D and innovation can not be separated from communication, and the inspection requirements of rubber hose have been improved compared with the previous ones. The storage site shall be free of ozone, heat source and equipment generating electromagnetic field. The coiled hoses or hose assemblies shall be stored horizontally, and the stacking height shall be limited to the extent that the products at the bottom will not produce permanent deformation.

high quality Acetylene pipe 1. During the molding of rubber products, the cohesive force of the elastomer cannot be eliminated due to the large pressure pressing. During the molding and mold release, extremely unstable shrinkage (the shrinkage rate of rubber varies due to different rubber types) often occurs. It must take a period of time before it can be gentle and stable. Therefore, at the beginning of the design of a rubber product, no matter the formula or the mold, it is necessary to carefully calculate the matching. If not, it is easy to cause dimensional instability of the product, resulting in low product quality. 2. Rubber belongs to thermosetting elastomer, while plastic belongs to thermosetting elastomer. Due to different sulfide types, the temperature range of rubber molding and curing is quite different, even affected by climate change and indoor temperature and humidity. Therefore, the production conditions of rubber products need to be properly adjusted at any time. If not, there may be differences in product quality. 3. The rubber product is the rubber mixture made from rubber raw materials after mixing in the internal mixer as the raw material. The formula is designed according to the characteristics of the required rubber products during mixing, and the required product hardness is determined. The product is molded by the rubber plate vulcanizer. After the product is formed, flash processing shall be carried out to make the product surface smooth without burrs. 4. The aging test of rubber products belongs to the category of aging test. Rubber aging refers to the phenomenon that the performance and structure of rubber and products are changed due to the combined effect of internal and external factors in the process of processing, storage and use, thus losing their use value. Acetylene pipe Price It is characterized by cracking, tackiness, hardening, softening, chalking, discoloration, mildew, etc. The following conditions shall be met when the ball mill uses the rubber lining plate: 1. The hardness of the ground material. The iron base alloy is similar to the rubber lining plate for materials below medium hardness, and the rubber lining plate is superior for materials above medium hardness. 2. The temperature of rubber lining plate is generally 70 ℃ - 90 ℃, and it can reach 110-130 ℃ under special circumstances. The temperature should be lower during dry grinding. 3. Feed size. Generally, the ball mill shall be more than 20-25mm; For the autogenous mill, the feeding particle size can be larger because no steel ball is added.

For the woodworking industry, many users high quality Acetylene pipe Not unfamiliar, this is an industrial dust collector used on woodworking carving machines, mainly used to absorb wood chips, wood ash, etc. At present, there are many kinds of woodworking vacuum tubes on the market. In the past few years, major furniture factories used PVC steel wire hoses with flat ends. In recent years, more and more enterprises have replaced cheap PVC steel wire hoses with more wear-resistant and durable pu steel wire expansion tubes. Some of the former take a few days or a month, while some of the latter take a few months or a year, They are also steel wire hoses. Why is the service life gap so far? First of all, you may have the impression that many PVC hoses have a very bad smell. This kind of hose is often used in daily life. Because the raw material itself is very cheap, the price of the finished product is also very low. For example, only a dozen yuan a piece. Think about the price of PVC raw materials, which is generally 8-15 yuan a kilogram, And most businesses will not use expensive PVC raw materials, Acetylene pipe Price The woodworking vacuum tube produced in this way has a very strong smell, not only unpleasant, but also many times the product can not even achieve environmental protection. However, the current updated product, pu steel wire telescopic tube, is a large woodworking furniture factory. An expensive woodworking carving machine uses a cheap vacuum tube with a very smelly smell, which has much to do with the overall style.

The hard core method adopts the core extrusion process to extrude the inner rubber tube blank, which directly uses the extruder to cover the inner rubber tube blank on the iron core, instead of the traditional casing process, and simplifies the process flow. Changzhou Acetylene pipe The billet forming adopts the process method of intertwining outer film and steel wire braiding forming. Similar to wrapping water wrapped cloth, the overlapping width is 1/2 of the film width. This process method can replace the method of wrapping outer film by extruder or by hand, reducing energy consumption and cost. We all know that the reinforcing layer and reinforcing layer of the rubber hose are the main force bearing parts, which are used to bear the load pressure. The factors determining the stress condition of the reinforced layer of the rubber hose are determined by the tension of the braided steel wire and the braiding angle. The high-speed steel wire hose braiding machine developed by our factory has introduced the advanced technology of foreign braiding production lines, and integrated the characteristics of domestic braiding machines. It integrates the advanced functions of hydraulic brake hose braiding production line, such as horizontal mechanical transmission, automatic lubrication, and so on, to develop equipment with high productivity and high degree of automation. The range of braiding diameter can be achieved Ф 6— Ф 25 Long core rubber hose (reinforcement layer). It fills the gap of domestic knitting production equipment, which can be widely used in rubber and plastic hose, rubber hose (reinforcement layer) knitting production equipment. The structure of high-pressure rubber hose is composed of four parts: inner liner, inner rubber layer, skeleton layer, middle rubber layer and outer rubber layer. Acetylene pipe Price In case of direct contact with the conveying medium, the synthetic rubber with good medium resistance, high tensile strength, high constant tensile stress, small compression permanent deformation and easy processing is usually selected. In order to meet the use requirements of strong polar medium resistance, the inner liner is composed of polytetrafluoroethylene layer and rubber layer, and a layer of film or adhesive is added on the surface of the inner liner to improve the adhesion with the skeleton material.