Rubber hose Price It has become the standard configuration of the modern new ball mill, but many problems may occur during the use or installation of the rubber lining plate, which will cause the failure of the rubber lining plate of the ball mill. Here is a brief introduction to the causes of the more common failure of the rubber lining plate of the ball mill. The design and installation are not professional and reasonable. The design and installation are also common problems for many novice manufacturers. For example, the bolt holes for fixing the ball mill lining plate are square, which will cause stress concentration and fracture. Adjust the size of lining plate to control the gap between lining plates at about 8mm; The installation quality of lining plate is very important to the safe operation of ball mill. First, tighten the fixed wedge symmetrically, put the lining plate in sequence, and then use the tightening wedge to secure it; Therefore, professional installation guidance can easily avoid these problems. The reason why the rubber lining plate of the ball mill does not match the steel ball is relatively common, and it is easy for many novice manufacturers to ignore and make mistakes. During the operation of the ball mill, the rubber lining plate of the ball mill, materials and steel balls promote the normal grinding and crushing of the ball mill due to the interaction of forces. The hardness of materials is related to wear resistance, and the wear resistance increases with the increase of hardness, Xiamen Rubber hose It is a pair of friction pairs, and the increase of hardness of one side will cause the wear of the other side to increase. Therefore, the high wear-resistant rubber lining plate is matched with the high wear-resistant steel ball, and the low wear-resistant rubber lining plate is matched with the low wear-resistant steel ball, so as to ensure the normal wear of the rubber lining plate of the ball mill and extend the service life of the ball mill.

Xiamen Rubber hose It is mainly used for the transportation of liquid and gas. The use requirements of cloth clip sand blasting pipe are stricter than those of ordinary rubber hose. The so-called high voltage puts forward this requirement. The following small series will introduce the use requirements of cloth clip sandblasting pipe. According to the use characteristics of cloth clip sand blasting pipe, the larger working pressure of cloth clip sand blasting pipe is determined according to the system pressure. Each cloth clamping sand blasting pipe has a normal working pressure, and the bursting pressure of cloth clamping sand blasting pipe is 3-4 times of the larger working pressure. The higher the pressure, the higher the number of steel wire layers, and the more stringent the product production. Therefore, according to the actual pressure of the system, the higher the working pressure of the cloth clamping sand blasting pipe, the normal operation of the system can be ensured, and the appropriate cloth clamping sand blasting pipe can be selected. If the impact pressure of the system is frequent, the cloth clip sandblasting pipe with high pulse life shall be selected, and the specification and model classification of the cloth clip sandblasting pipe shall be properly improved. Temperature is also one of the factors considered by customers. Rubber hose Price The high and low temperature transition in the working environment will affect the service life and pressure bearing capacity of the rubber hose. Therefore, high-pressure rubber hoses should be used within their allowable range. For the system whose long-term operating temperature is not within its allowable range, hose sheath or special rubber hose shall be purchased.

Xiamen Rubber hose Also called rubber hose for sand blasting. It is suitable for air pressure sand blasting of metal surface for rust removal, hemp removal, and sand blasting rubber hose for wet sand blasting and dry sand blasting in engineering construction. It is suitable for air pressure sand blasting of metal surface for rust removal, hemp removal, and sand blasting rubber hose for wet sand blasting and dry sand blasting in engineering construction. The common application fields are shipbuilding, machining, spraying industry, etc. Appearance of abrasion resistant sand blasting rubber hose: 1. Light abrasion resistant sand blasting rubber hose consists of black, yellowish or transparent abrasion resistant rubber inner layer, central fabric or cord reinforcement layer, medium rubber layer and outer rubber layer; 2. Heavy abrasion resistant rubber hose consists of black, yellowish or transparent abrasion resistant rubber inner layer, cloth clip or cord reinforcement layer, steel wire framework reinforcement layer, medium rubber layer Composition of outer rubber layer 3. The steel wire braided wear-resistant sandblasting hose is composed of black, yellowish or transparent wear-resistant rubber inner layer, single-layer or multi-layer steel wire braided reinforcement layer, medium rubber layer and outer rubber layer. Purpose Abrasion resistant sand blasting hose is a kind of material conveying pipe, which is mainly used for conveying solids containing particles such as particles, gravel, cement, quicksand, mud, gypsum, etc. It is suitable for various tunnel projects, tunnels, caverns and other engineering operations. The general working pressure is less than 12 bar, and the higher bursting pressure can reach 36 bar. Sometimes the vacuum rich negative pressure parameter is 0.8 bar 0.9 bar. Rubber hose Price Hydraulic requirements 1. The maximum working pressure of wear-resistant sand blasting hose is 0.63MPa. 2. The hose shall be free from water seepage, local bulge, expansion and other abnormalities when conducting hydraulic test under twice the working pressure. Keep the pressure of anti-static hose for 1min, and the length change shall not exceed ± 0.8%, the outer diameter change shall not exceed ± 10%, and the torsion per meter shall not exceed 60 º. 3. The bursting pressure of the hose shall not be less than 4 times of the working pressure.

Xiamen Rubber hose The break of the sandblasting hose usually refers to the appearance and change of the crack of the sandblasting hose. The sandblasting hose has one or more cracks, but the cracks are neat. Another is that the internal bending cracks at the crack of the sandblasting hose are neat. The causes of different errors are different, and the treatment methods are also different. Therefore, in the process of using or protecting the sandblasting hose, the sandblasting hose should not be subject to changing torque. When installing the sandblasting hose, try to keep the axis of the two joints on the same plane to avoid twisting the sandblasting hose in use. Therefore, be careful with the application, and try not to make the sandblasting hose change excessively to avoid consumption. Sand blasting hose plays a very important role in the industry. Its inner rubber layer is added with carbon black, which can effectively eliminate static electricity and directly contact with compressed air and abrasives. The requirement for wear resistance is quite high. Once worn through, the reinforcement layer will be exposed, and the sand blasting hose will burst. The reinforcing layer of sandblasting hose is a pressure resistant layer, so wear-resisting Rubber hose The material and layout of the reinforcement layer directly determine the pressure rating of the sandblasting hose. There are two common enhancement layers: cloth clip enhancement layer and surround enhancement layer. The sand blasting hose with an inner diameter of 50mm or more is mostly used in the construction occasions where the sand blasting pipe needs to be extended to reduce the pressure loss in the sand blasting hose and ensure the normal operation of shot blasting.

1. Mutual wear of rubber lining plate and steel ball of ball mill: both the rubber lining plate and steel ball of ball mill are vulnerable parts. During grinding, the steel ball and material of ball mill do throw line falling movement in the barrel Xiamen Rubber hose It will collide with steel balls and materials and cause friction. In continuous operation, the rubber lining plate and steel ball of ball mill will be severely worn, which is directly related to the hardness of materials. The greater the hardness of the material, the faster the abrasion speed of the rubber lining plate and steel ball of the ball mill, which may cause equipment damage or even safety accidents in serious cases. In addition, it is also related to the ball of the ball mill. The size and quantity of the ball will affect the service life of the rubber lining plate of the ball mill. If the ball mill is in operation, increasing the amount of steel balls or filling steel balls with larger diameters will increase the wear of the rubber lining plate of the ball mill. 2. The heat treatment process of the rubber lining plate of the ball mill is unreasonable: the unreasonable heat treatment of the rubber lining plate of the ball mill will not only increase the wear of the lining plate, but also affect the yield strength of the lining plate, resulting in the fracture of the bolt of the ball mill under the large shear force. In the actual operation, the staff lacked the understanding of the lining plate material and the heat treatment processing of the ball mill rubber lining plate was insufficient, so the strengthening effect of the ball mill rubber lining plate was not in place and the strength was low. When impacted by steel balls and materials, Rubber hose Price Plastic deformation often occurs. 3. The material of the rubber lining plate of the ball mill is unreasonable: the material of the rubber lining plate of the ball mill and its heat treatment process are the key to determine the mechanical performance of the lining plate. If the material of the lining plate is not properly selected, its fatigue strength and life will be greatly reduced, which will not meet the requirements of the ball mill, or even plastic deformation or bulge will occur.

1. The use of protection cannot be ignored: the long-term use of high-pressure sand blasting hose joints at home usually does not cause concern, but excessive use and improper protection also buried the hidden danger of joint cracking to a certain extent. It is understood that the service life of the joint is usually 200000 times, and it should be replaced after long-term use. When using the side, Rubber hose Price Care should be taken to close and open as gently as possible and not to rotate the knob of the hose connector repeatedly. 2. Differentiation of quality can be based on standard evidence collection. It is understood that it is still difficult to determine the cause of joint cracking. At present, the National Bureau of Technology and Quality Supervision has issued recommendations for sealing nozzles and hose specifications. These two specifications perfectly adjust the quality specification target of connectors and hoses. Consumers can go to the quality inspection department to check the torsional strength of the connecting hose, the tightness of the connecting spool and the strength of the connecting materials. If the content of standard rules cannot be met, it will be attributed to quality problems, which can serve as a strong basis for expression. 3. The appearance of hose connector is difficult to distinguish between good and bad. In order to pursue profits and reduce costs, many manufacturers currently use selected cast iron (easy to rust) and zinc alloy (non anti-corrosion) as materials to produce high-pressure sand blasting hose joints, which causes product quality problems. It is understood that the quality of connectors and hoses is not up to standard, Xiamen Rubber hose The strength function and sealing function of high-pressure sand blasting hose joints are not up to standard due to problems such as materials and wall thickness, which should be paid attention to by consumers.