one Yinchuan Rubber hose When using, the talcum powder on the inner wall of the hose must be blown clean to prevent the channel of the welding torch from being blocked. Avoid external extrusion and mechanical damage during use, and do not fold the pipe body. 2. Care must be taken when storing and using the hose to keep it clean and free from damage. For example, avoid exposure to sunlight, rain and snow, and prevent contact with acids, alkalis, oils and other organic solvents that can damage the hose. The storage temperature shall be - 15~40 ℃, and the distance from the heat source shall not be less than 1m. 3. According to the national standards, the oxygen hose is red, the working pressure vessel is 1.5MPa, the inner diameter of the hose is 8mm, and the outer diameter is 18mm; The acetylene hose is black, the working pressure vessel is 0.3MPa, the inner diameter of the hose is 8mm, and the outer diameter is 16mm. 4. The gas cutting operation requires a large oxygen output, so the valves of the gas cylinder (or oxygen pipeline) connected to the high pressure end of the oxygen meter should be fully opened to ensure adequate flow and stable pressure. The low pressure gauge has indicated the working pressure, but the pressure drops suddenly when using oxygen. At this time, it is easy to backfire and may backfire into the oxygen hose to cause explosion. 5. Oxygen hose and acetylene hose shall not be mixed or substituted with each other, and oxygen and hose shall not be used to blow away the blockage of acetylene hose. At the same time, it is necessary to check and eliminate the defects such as gas leakage and blockage of the welding torch at any time to prevent the formation of oxygen and acetylene mixture in the hose. It should be pointed out that the hose color specified in the national standard is opposite to that specified in the international standard (ISO) (oxygen hose is black, acetylene hose is red). At the same time, it is different from the original ministerial standard (HG4-605-66) that oxygen hose is red and acetylene hose is green. Before 1966, domestic oxygen hose was black or green and acetylene hose was red. thus Rubber hose Price It causes inconsistency between the understanding and habits of the supply department and the user, and is easy to cause accidents due to the mixing and substitution of rubber hoses. At present, it should be emphasized that unified understanding and use should be carried out in accordance with the provisions of national standards, and attention should be paid to distinguishing the rubber hoses of imported equipment.
production Rubber hose The inner rubber layer of（ ф 0.3-2.0 reinforcement layer) is the skeleton material that plays the role of reinforcement. What should be paid attention to when storing the wear-resistant sandblasting pipe. 1. The wear-resistant sandblasting pipe should be stored as loose as possible. Generally, rubber hoses with inner diameter less than 76 mm can be wound and stored. 2. During the storage of wear-resistant sand blasting pipe, it is strictly prohibited to stack heavy objects on the pipe body to prevent external extrusion and damage. 3. During the storage of wear-resistant sand blasting pipe, do not contact with acid, alkali, oil, organic solvent or other corrosive liquids and gases, and the heat release should start from 1m away. 4. The storage period of wear-resistant sand blasting pipe shall not exceed 2 years, and it shall be used by the first person to prevent the quality of rubber pipe from being affected by long-term storage. 5. When wear-resistant sand blasting pipes need to be temporarily stored in the open air, the site should be flat and the rubber pipe should be laid flat. The upper cover should be placed under the rubber pipe and no heavy objects should be stacked. At the same time, the hose shall not contact the heat source. 6. The storage place of the upper and lower rubber pipes in the well shall be kept clean and ventilated, and the relative humidity shall be 80. The temperature of the storage place shall be kept between - 15 ℃ and 40 ℃, and the rubber pipe shall be protected from direct sunlight and water spray. 7. When storing wear-resistant sand blasting pipe, Rubber hose Price Both ends of the hose shall be sealed firmly to prevent sundries from entering the hose. 8. When the wear-resistant sand blasting pipe is stored, it should be placed separately according to different varieties and specifications, not mixed, and hang the management board. 9. In order to prevent the pipes from being pressed and deformed during storage, they should not be stacked too high, and the stacking height should not exceed 1.5m. It also requires rubber hoses to be "stacked" frequently during storage, at least once a quarter.
Yinchuan Rubber hose Structure type of product: sand blasting hose is mainly composed of liquid resistant inner rubber layer, middle rubber layer, 2 or 4 or 6 layers of steel wire winding reinforcement layer and outer rubber layer. The inner rubber layer has the function of bearing the pressure of the transmission medium and protecting the steel wire from erosion, the outer rubber layer protects the steel wire from damage, and the steel wire (0.3-2.0 steel wire) layer is the reinforced skeleton material. Application of sandblasting hose products: high-pressure sandblasting hose is mainly used for mining hydraulic support and oil field exploitation, and is suitable for engineering construction, lifting and transportation, metallurgical forging, mining equipment, ships, injection molding machinery, agricultural machinery, various machine tools, and mechanical and automatic hydraulic systems in various industrial sectors to transport petroleum base with a certain pressure (higher pressure) and temperature. (such as mineral oil, soluble oil, hydraulic oil, fuel oil, lubricating oil) and water-based liquid (such as emulsion, oil-water emulsion, water). And liquid transmission. The working withstand voltage can reach 70-100 MPa. The company's sand blasting hose standards refer to national standards/T10544-03, DIN 20023, and SaE100 R9-13. Rubber hose Price Made of special synthetic rubber, it has excellent oil resistance, heat resistance and aging resistance. The rubber hose has high bearing pressure and superior pulse performance. The tube body is tightly combined, soft to use, and has little compression deformation. The hose has excellent bending resistance and fatigue resistance. The sandblasting hose is 20m long and can be made within 50m as required.
Yinchuan Rubber hose Vulcanization of technical performance indicators is an important process to enhance the adhesive strength between rubber and reinforcement layer and make it a whole in rubber hose manufacturing, and also an important link to ensure and improve product quality. In order to obtain good pulse performance and service performance of steel wire reinforced rubber hose, in addition to reasonable structure and formula, it is necessary to ensure the compactness of vulcanized hose. In order to meet this performance requirement, the traditional vulcanization method is to wrap the water in water cloth on the semi-finished hose before vulcanization, make braided hose or steel wire for reinforcement and fastening, and vulcanize in batches with steam vulcanization tank. Since the performance requirements of medium and low pressure hoses are low, the rubber hose can also be directly put into the curing tank without fastening. Although water wrapped cloth vulcanization can also increase the compactness of the hose, its appearance is poor. In order to obtain the smooth outer surface of the hose, the lead coating vulcanization method is widely used at home and abroad. For decades, people have been using this method as an effective method to vulcanize and strengthen rubber hoses, especially high-pressure rubber hoses. So far, many domestic and foreign manufacturers are still using this method to produce rubber hoses. But the fatal disadvantage of this method is that it pollutes the environment. Rubber hose Price The main control function of the air compressor station unit is to exhaust more air. According to different structures, it can be divided into full hose, cloth hose, steel braided hose, etc. According to different uses, it can be divided into air hose, water suction hose, water delivery hose, heat resistant hose, acid (alkali) resistant hose, oil resistant hose and special hose., It can be closed within the specified range.
The air conditioning in the hall of a giant building is provided by the 6FWB unit fixed in the basement. production Rubber hose The vibration of the unit is transmitted to the ground hall through the bridge connecting the sand blasting hose pipe, and the noise value reaches 45dB. In such an environment, people always feel uncomfortable. After the improved design, sandblasting rubber pipes were connected in series on the connecting pipes, which not only absorbed some of the noise generated by the unit vibration, but also the noise generated by the fluid pulsation in the pipeline system. At this time, the noise value in the ground hall was only 33dB, greatly improving the environment in the hall. The movable cylinder on the vulcanizing press will move upward and downward for the need of loading and unloading the mold. After repeated reciprocating movements, the copper serpentine will suffer from fatigue fracture. Although it can still be used after repair, it will cause time loss if it is stopped for repair. Rubber hose Price Although it has good soft properties and strong fatigue resistance, it is weak in pressure bearing, temperature resistance, aging resistance and other aspects, and can not continue after several months of use. The good comprehensive performance of sand blasting hose is fully reflected here. In the general industrial field, in addition to pressure and temperature, there are often severe conditions such as fatigue, corrosion, vibration, compression, impact, etc. Under such circumstances, it is most appropriate to use sandblasting hose to compensate for the position movement of the pipeline.
production Rubber hose 1. During the molding of rubber products, the cohesive force of the elastomer cannot be eliminated due to the large pressure pressing. During the molding and mold release, extremely unstable shrinkage (the shrinkage rate of rubber varies due to different rubber types) often occurs. It must take a period of time before it can be gentle and stable. Therefore, at the beginning of the design of a rubber product, no matter the formula or the mold, it is necessary to carefully calculate the matching. If not, it is easy to cause dimensional instability of the product, resulting in low product quality. 2. Rubber belongs to thermosetting elastomer, while plastic belongs to thermosetting elastomer. Due to different sulfide types, the temperature range of rubber molding and curing is quite different, even affected by climate change and indoor temperature and humidity. Therefore, the production conditions of rubber products need to be properly adjusted at any time. If not, there may be differences in product quality. 3. The rubber product is the rubber mixture made from rubber raw materials after mixing in the internal mixer as the raw material. The formula is designed according to the characteristics of the required rubber products during mixing, and the required product hardness is determined. The product is molded by the rubber plate vulcanizer. After the product is formed, flash processing shall be carried out to make the product surface smooth without burrs. 4. The aging test of rubber products belongs to the category of aging test. Rubber aging refers to the phenomenon that the performance and structure of rubber and products are changed due to the combined effect of internal and external factors in the process of processing, storage and use, thus losing their use value. Rubber hose Price It is characterized by cracking, tackiness, hardening, softening, chalking, discoloration, mildew, etc. The following conditions shall be met when the ball mill uses the rubber lining plate: 1. The hardness of the ground material. The iron base alloy is similar to the rubber lining plate for materials below medium hardness, and the rubber lining plate is superior for materials above medium hardness. 2. The temperature of rubber lining plate is generally 70 ℃ - 90 ℃, and it can reach 110-130 ℃ under special circumstances. The temperature should be lower during dry grinding. 3. Feed size. Generally, the ball mill shall be more than 20-25mm; For the autogenous mill, the feeding particle size can be larger because no steel ball is added.