Air compression hose Where can I find it? It has become the standard configuration of the modern new ball mill, but many problems may occur during the use or installation of the rubber lining plate, which will cause the failure of the rubber lining plate of the ball mill. Here is a brief introduction to the causes of the more common failure of the rubber lining plate of the ball mill. The design and installation are not professional and reasonable. The design and installation are also common problems for many novice manufacturers. For example, the bolt holes for fixing the ball mill lining plate are square, which will cause stress concentration and fracture. Adjust the size of lining plate to control the gap between lining plates at about 8mm; The installation quality of lining plate is very important to the safe operation of ball mill. First, tighten the fixed wedge symmetrically, put the lining plate in sequence, and then use the tightening wedge to secure it; Therefore, professional installation guidance can easily avoid these problems. The reason why the rubber lining plate of the ball mill does not match the steel ball is relatively common, and it is easy for many novice manufacturers to ignore and make mistakes. During the operation of the ball mill, the rubber lining plate of the ball mill, materials and steel balls promote the normal grinding and crushing of the ball mill due to the interaction of forces. The hardness of materials is related to wear resistance, and the wear resistance increases with the increase of hardness, Chengdu Air compression hose It is a pair of friction pairs, and the increase of hardness of one side will cause the wear of the other side to increase. Therefore, the high wear-resistant rubber lining plate is matched with the high wear-resistant steel ball, and the low wear-resistant rubber lining plate is matched with the low wear-resistant steel ball, so as to ensure the normal wear of the rubber lining plate of the ball mill and extend the service life of the ball mill.

1. Mutual wear of rubber lining plate and steel ball of ball mill: both the rubber lining plate and steel ball of ball mill are vulnerable parts. During grinding, the steel ball and material of ball mill do throw line falling movement in the barrel Chengdu Air compression hose It will collide with steel balls and materials and cause friction. In continuous operation, the rubber lining plate and steel ball of ball mill will be severely worn, which is directly related to the hardness of materials. The greater the hardness of the material, the faster the abrasion speed of the rubber lining plate and steel ball of the ball mill, which may cause equipment damage or even safety accidents in serious cases. In addition, it is also related to the ball of the ball mill. The size and quantity of the ball will affect the service life of the rubber lining plate of the ball mill. If the ball mill is in operation, increasing the amount of steel balls or filling steel balls with larger diameters will increase the wear of the rubber lining plate of the ball mill. 2. The heat treatment process of the rubber lining plate of the ball mill is unreasonable: the unreasonable heat treatment of the rubber lining plate of the ball mill will not only increase the wear of the lining plate, but also affect the yield strength of the lining plate, resulting in the fracture of the bolt of the ball mill under the large shear force. In the actual operation, the staff lacked the understanding of the lining plate material and the heat treatment processing of the ball mill rubber lining plate was insufficient, so the strengthening effect of the ball mill rubber lining plate was not in place and the strength was low. When impacted by steel balls and materials, Air compression hose Where can I find it? Plastic deformation often occurs. 3. The material of the rubber lining plate of the ball mill is unreasonable: the material of the rubber lining plate of the ball mill and its heat treatment process are the key to determine the mechanical performance of the lining plate. If the material of the lining plate is not properly selected, its fatigue strength and life will be greatly reduced, which will not meet the requirements of the ball mill, or even plastic deformation or bulge will occur.

As production Air compression hose As an important part of sand blasting machinery, its safety plays a vital role in the safety of equipment operation. The following will briefly analyze the precautions in the use of high-pressure sandblasting pipe: I. Pipe inner diameter: inner diameter of high-pressure sandblasting pipe. 2、 Attention shall be paid to the following items in the use and design of high-pressure sandblasting pipe: 1. The bending radius of high-pressure sandblasting pipe shall not be too small, and generally shall not be less than the value specified in the assembly technology of high-pressure sandblasting pipe. The joint between the high-pressure sandblasting pipe assembly and the pipe joint shall have a straight section, and its length shall not be less than twice the outer diameter of the pipe. 2. The length of high-pressure rubber hose assembly shall consider that the high-pressure rubber hose will shrink and deform after introducing pressure oil. Generally speaking, the shrinkage rate is 3~4 times of the pipe length. When installing the high-pressure rubber hose assembly, it is not allowed to bear tension. 3. During installation, the high-pressure sandblasting pipe assembly shall be free from torsional deformation. Air compression hose Where can I find it? The connecting shaft of shall be placed in the moving plane as far as possible to avoid damaging the high-pressure sandblasting pipe when both ends move with each other. 4. High pressure resistant sand blasting pipe shall avoid contact and friction with mechanical sharp corners to avoid damaging the pipe. Safety measures: to ensure the safe and reliable use of high-pressure sandblasting pipe assembly.

Due to the limitation of spatial location conditions, production Air compression hose The installation stress of can often bring various difficulties to the installation work: formed pipes cannot be installed; When you bend down, you are about to come. If you make do with pipes, local cold correction will inevitably occur. According to the size of the pipeline and the specific situation on site, the cold correction amount varies from several millimeters to tens of millimeters, some as high as hundreds of millimeters. Practice has proved that the greater the quantity, the higher the internal stress. These residual installation stresses in the rubber sand blasting pipe are undoubtedly huge hidden information. The lubricating oil duct of a certain type of engine bearing was broken for many times due to excessive installation stress in actual operation. Because it can be bent at will, the internal stress generated by bending under the condition of rated bending radius is very small, which brings great convenience to the installation work, and also plays a certain role in ensuring the safe operation of the rubber sand blasting pipe. This is the main reason why some rubber sand blasting pipes must be used. Since it is necessary to load and unload the mold, the movable cylinder on the vulcanizer will move up and down. After repeated reciprocation, the copper serpentine tube will undergo fatigue fracture. Although it can continue to be used after repair, stopping for repair will cause time loss. Chengdu Air compression hose Although it has good flexibility and strong fatigue resistance, it is also weak in pressure bearing, temperature resistance, aging resistance and other aspects, and can not be used after several months. The good comprehensive performance of rubber sand blasting pipe is fully reflected here.

The hard core method adopts the core extrusion process to extrude the inner rubber tube blank, which directly uses the extruder to cover the inner rubber tube blank on the iron core, instead of the traditional casing process, and simplifies the process flow. Chengdu Air compression hose The billet forming adopts the process method of intertwining outer film and steel wire braiding forming. Similar to wrapping water wrapped cloth, the overlapping width is 1/2 of the film width. This process method can replace the method of wrapping outer film by extruder or by hand, reducing energy consumption and cost. We all know that the reinforcing layer and reinforcing layer of the rubber hose are the main force bearing parts, which are used to bear the load pressure. The factors determining the stress condition of the reinforced layer of the rubber hose are determined by the tension of the braided steel wire and the braiding angle. The high-speed steel wire hose braiding machine developed by our factory has introduced the advanced technology of foreign braiding production lines, and integrated the characteristics of domestic braiding machines. It integrates the advanced functions of hydraulic brake hose braiding production line, such as horizontal mechanical transmission, automatic lubrication, and so on, to develop equipment with high productivity and high degree of automation. The range of braiding diameter can be achieved Ф 6— Ф 25 Long core rubber hose (reinforcement layer). It fills the gap of domestic knitting production equipment, which can be widely used in rubber and plastic hose, rubber hose (reinforcement layer) knitting production equipment. The structure of high-pressure rubber hose is composed of four parts: inner liner, inner rubber layer, skeleton layer, middle rubber layer and outer rubber layer. Air compression hose Where can I find it? In case of direct contact with the conveying medium, the synthetic rubber with good medium resistance, high tensile strength, high constant tensile stress, small compression permanent deformation and easy processing is usually selected. In order to meet the use requirements of strong polar medium resistance, the inner liner is composed of polytetrafluoroethylene layer and rubber layer, and a layer of film or adhesive is added on the surface of the inner liner to improve the adhesion with the skeleton material.