wear-resisting Air compression hose 1. During the molding of rubber products, the cohesive force of the elastomer cannot be eliminated due to the large pressure pressing. During the molding and mold release, extremely unstable shrinkage (the shrinkage rate of rubber varies due to different rubber types) often occurs. It must take a period of time before it can be gentle and stable. Therefore, at the beginning of the design of a rubber product, no matter the formula or the mold, it is necessary to carefully calculate the matching. If not, it is easy to cause dimensional instability of the product, resulting in low product quality. 2. Rubber belongs to thermosetting elastomer, while plastic belongs to thermosetting elastomer. Due to different sulfide types, the temperature range of rubber molding and curing is quite different, even affected by climate change and indoor temperature and humidity. Therefore, the production conditions of rubber products need to be properly adjusted at any time. If not, there may be differences in product quality. 3. The rubber product is the rubber mixture made from rubber raw materials after mixing in the internal mixer as the raw material. The formula is designed according to the characteristics of the required rubber products during mixing, and the required product hardness is determined. The product is molded by the rubber plate vulcanizer. After the product is formed, flash processing shall be carried out to make the product surface smooth without burrs. 4. The aging test of rubber products belongs to the category of aging test. Rubber aging refers to the phenomenon that the performance and structure of rubber and products are changed due to the combined effect of internal and external factors in the process of processing, storage and use, thus losing their use value. Air compression hose company It is characterized by cracking, tackiness, hardening, softening, chalking, discoloration, mildew, etc. The following conditions shall be met when the ball mill uses the rubber lining plate: 1. The hardness of the ground material. The iron base alloy is similar to the rubber lining plate for materials below medium hardness, and the rubber lining plate is superior for materials above medium hardness. 2. The temperature of rubber lining plate is generally 70 ℃ - 90 ℃, and it can reach 110-130 ℃ under special circumstances. The temperature should be lower during dry grinding. 3. Feed size. Generally, the ball mill shall be more than 20-25mm; For the autogenous mill, the feeding particle size can be larger because no steel ball is added.

wear-resisting Air compression hose Acid and alkali resistance: there is no obvious change after soaking in 44 solutions for 24 hours; Pressure resistance: under the pressure of 52.5 MPa, the pressure is stable for 5 minutes without leakage, the surface of the pipe body is not deformed, and the damage pressure is greater than 105 MPa; Heat preservation: place the pipe in an environment of 300-50 ℃, with clear water in the pipe for 20 minutes, and the temperature ratio inside and outside the pipe is 1:40. The wear-resistant sand blasting hose is a material conveying pipe. The wear-resistant sand blasting hose is a material conveying pipe. Common black, yellowish or transparent; Most of them are wrapped by external rubber packing belt, and the steel wire is usually set between the internal and external rubber for negative pressure operation. The utility model is mainly used for conveying liquid containing solid particles such as particles, gravel, cement, quicksand, concrete, gypsum, etc., and is suitable for various tunnel projects, shafts, tunnels, and other engineering operations. The inner rubber and outer rubber of sand blasting pipe made of ordinary materials are usually made of wear-resistant materials, most of which are nitrile rubber (acrylonitrile butadiene copolymer), styrene butadiene rubber (oil extended styrene butadiene rubber), etc., Or PARA rubber (trefoil rubber), the inlet hose has better performance. According to the working conditions and the degree of loss of material particles to the transmission medium, the sand blasting pipe is generally divided into light sand blasting pipe and heavy sand blasting pipe. Spiral wire will make them suitable for negative pressure environment. Light sandblasting pipe Light sandblasting pipe Light sandblasting pipe is usually used in marine sandblasting and quicksand operations. The ordinary inner rubber is made of wear-resistant nitrile rubber (NBR), while the outer rubber is wrapped with composite rubber. Heavy sandblasting pipe Heavy sandblasting pipe Heavy sandblasting pipe is used for sandblasting sand, pebble, mud, etc. Equipment. Air compression hose company Sand blasting vacuum tube Sand blasting vacuum tube The sand blasting vacuum tube is embedded with spiral steel wire, and the general vacuum negative pressure can reach 0.9 bar. Common parameter definitions The wear-resistant sandblasting pipe generally has the following parameters: folding pressure is generally within 12 bar, higher sandblasting pressure can reach 36 bar, and sometimes vacuum negative pressure parameters such as 0.8 bar~0.9 bar are required.

1. The use of protection cannot be ignored: the long-term use of high-pressure sand blasting hose joints at home usually does not cause concern, but excessive use and improper protection also buried the hidden danger of joint cracking to a certain extent. It is understood that the service life of the joint is usually 200000 times, and it should be replaced after long-term use. When using the side, Air compression hose company Care should be taken to close and open as gently as possible and not to rotate the knob of the hose connector repeatedly. 2. Differentiation of quality can be based on standard evidence collection. It is understood that it is still difficult to determine the cause of joint cracking. At present, the National Bureau of Technology and Quality Supervision has issued recommendations for sealing nozzles and hose specifications. These two specifications perfectly adjust the quality specification target of connectors and hoses. Consumers can go to the quality inspection department to check the torsional strength of the connecting hose, the tightness of the connecting spool and the strength of the connecting materials. If the content of standard rules cannot be met, it will be attributed to quality problems, which can serve as a strong basis for expression. 3. The appearance of hose connector is difficult to distinguish between good and bad. In order to pursue profits and reduce costs, many manufacturers currently use selected cast iron (easy to rust) and zinc alloy (non anti-corrosion) as materials to produce high-pressure sand blasting hose joints, which causes product quality problems. It is understood that the quality of connectors and hoses is not up to standard, Xingtai Air compression hose The strength function and sealing function of high-pressure sand blasting hose joints are not up to standard due to problems such as materials and wall thickness, which should be paid attention to by consumers.

Xingtai Air compression hose The break of the sandblasting hose usually refers to the appearance and change of the crack of the sandblasting hose. The sandblasting hose has one or more cracks, but the cracks are neat. Another is that the internal bending cracks at the crack of the sandblasting hose are neat. The causes of different errors are different, and the treatment methods are also different. Therefore, in the process of using or protecting the sandblasting hose, the sandblasting hose should not be subject to changing torque. When installing the sandblasting hose, try to keep the axis of the two joints on the same plane to avoid twisting the sandblasting hose in use. Therefore, be careful with the application, and try not to make the sandblasting hose change excessively to avoid consumption. Sand blasting hose plays a very important role in the industry. Its inner rubber layer is added with carbon black, which can effectively eliminate static electricity and directly contact with compressed air and abrasives. The requirement for wear resistance is quite high. Once worn through, the reinforcement layer will be exposed, and the sand blasting hose will burst. The reinforcing layer of sandblasting hose is a pressure resistant layer, so wear-resisting Air compression hose The material and layout of the reinforcement layer directly determine the pressure rating of the sandblasting hose. There are two common enhancement layers: cloth clip enhancement layer and surround enhancement layer. The sand blasting hose with an inner diameter of 50mm or more is mostly used in the construction occasions where the sand blasting pipe needs to be extended to reduce the pressure loss in the sand blasting hose and ensure the normal operation of shot blasting.

I believe everyone is familiar with wear-resisting Air compression hose Relevant application knowledge of products. It is understood that at present, this product is mainly used for mining hydraulic support and oilfield development. It is applicable to engineering construction, lifting transportation, metallurgical forging, mining equipment, ships, injection molding machinery, agricultural machinery, various machine tools, mechanization of various industrial departments, water-based liquids, etc. And liquid transmission. Its relatively high working pressure can reach 70-120 MPa. In order to achieve better application effect, what problems should be paid attention to when using high-pressure braided hose? 1. The bending radius shall not be less than the given bending radius to prevent damage to the hose skeleton or premature failure due to excessive tension. 2. Select the type and specification of the hose correctly according to the use conditions, and do not misuse or replace it. 3. When using high-pressure braided hose, the pressure should be adjusted slowly and evenly to avoid sudden pressure increase and damage to the pipe body. 4. When the work site changes, it should be removed from the ground without dragging, so as to avoid the skeleton layer being corroded after scratching the outer glue. 5. After delivering corrosive liquid, the interior should be cleaned to prevent residues from corroding the pipe body for a long time, or select corresponding series of products. When storing high-pressure braided rubber hoses, depending on the type of rubber used, Air compression hose company Note which conditions typically change over time. However, due to several factors or a combination of several factors, this change may accelerate, and other materials used to strengthen high-pressure braided hoses may also be adversely affected by improper storage conditions.

Xingtai Air compression hose It is mainly used for the transportation of liquid and gas. The use requirements of cloth clip sand blasting pipe are stricter than those of ordinary rubber hose. The so-called high voltage puts forward this requirement. The following small series will introduce the use requirements of cloth clip sandblasting pipe. According to the use characteristics of cloth clip sand blasting pipe, the larger working pressure of cloth clip sand blasting pipe is determined according to the system pressure. Each cloth clamping sand blasting pipe has a normal working pressure, and the bursting pressure of cloth clamping sand blasting pipe is 3-4 times of the larger working pressure. The higher the pressure, the higher the number of steel wire layers, and the more stringent the product production. Therefore, according to the actual pressure of the system, the higher the working pressure of the cloth clamping sand blasting pipe, the normal operation of the system can be ensured, and the appropriate cloth clamping sand blasting pipe can be selected. If the impact pressure of the system is frequent, the cloth clip sandblasting pipe with high pulse life shall be selected, and the specification and model classification of the cloth clip sandblasting pipe shall be properly improved. Temperature is also one of the factors considered by customers. Air compression hose company The high and low temperature transition in the working environment will affect the service life and pressure bearing capacity of the rubber hose. Therefore, high-pressure rubber hoses should be used within their allowable range. For the system whose long-term operating temperature is not within its allowable range, hose sheath or special rubber hose shall be purchased.