wear-resisting Air compression hose 1. During the molding of rubber products, the cohesive force of the elastomer cannot be eliminated due to the large pressure pressing. During the molding and mold release, extremely unstable shrinkage (the shrinkage rate of rubber varies due to different rubber types) often occurs. It must take a period of time before it can be gentle and stable. Therefore, at the beginning of the design of a rubber product, no matter the formula or the mold, it is necessary to carefully calculate the matching. If not, it is easy to cause dimensional instability of the product, resulting in low product quality. 2. Rubber belongs to thermosetting elastomer, while plastic belongs to thermosetting elastomer. Due to different sulfide types, the temperature range of rubber molding and curing is quite different, even affected by climate change and indoor temperature and humidity. Therefore, the production conditions of rubber products need to be properly adjusted at any time. If not, there may be differences in product quality. 3. The rubber product is the rubber mixture made from rubber raw materials after mixing in the internal mixer as the raw material. The formula is designed according to the characteristics of the required rubber products during mixing, and the required product hardness is determined. The product is molded by the rubber plate vulcanizer. After the product is formed, flash processing shall be carried out to make the product surface smooth without burrs. 4. The aging test of rubber products belongs to the category of aging test. Rubber aging refers to the phenomenon that the performance and structure of rubber and products are changed due to the combined effect of internal and external factors in the process of processing, storage and use, thus losing their use value. Air compression hose Price It is characterized by cracking, tackiness, hardening, softening, chalking, discoloration, mildew, etc. The following conditions shall be met when the ball mill uses the rubber lining plate: 1. The hardness of the ground material. The iron base alloy is similar to the rubber lining plate for materials below medium hardness, and the rubber lining plate is superior for materials above medium hardness. 2. The temperature of rubber lining plate is generally 70 ℃ - 90 ℃, and it can reach 110-130 ℃ under special circumstances. The temperature should be lower during dry grinding. 3. Feed size. Generally, the ball mill shall be more than 20-25mm; For the autogenous mill, the feeding particle size can be larger because no steel ball is added.

CiH Air compression hose Vulcanization of technical performance indicators is an important process to enhance the adhesive strength between rubber and reinforcement layer and make it a whole in rubber hose manufacturing, and also an important link to ensure and improve product quality. In order to obtain good pulse performance and service performance of steel wire reinforced rubber hose, in addition to reasonable structure and formula, it is necessary to ensure the compactness of vulcanized hose. In order to meet this performance requirement, the traditional vulcanization method is to wrap the water in water cloth on the semi-finished hose before vulcanization, make braided hose or steel wire for reinforcement and fastening, and vulcanize in batches with steam vulcanization tank. Since the performance requirements of medium and low pressure hoses are low, the rubber hose can also be directly put into the curing tank without fastening. Although water wrapped cloth vulcanization can also increase the compactness of the hose, its appearance is poor. In order to obtain the smooth outer surface of the hose, the lead coating vulcanization method is widely used at home and abroad. For decades, people have been using this method as an effective method to vulcanize and strengthen rubber hoses, especially high-pressure rubber hoses. So far, many domestic and foreign manufacturers are still using this method to produce rubber hoses. But the fatal disadvantage of this method is that it pollutes the environment. Air compression hose Price The main control function of the air compressor station unit is to exhaust more air. According to different structures, it can be divided into full hose, cloth hose, steel braided hose, etc. According to different uses, it can be divided into air hose, water suction hose, water delivery hose, heat resistant hose, acid (alkali) resistant hose, oil resistant hose and special hose., It can be closed within the specified range.

As wear-resisting Air compression hose As an important part of sand blasting machinery, its safety plays a vital role in the safety of equipment operation. The following will briefly analyze the precautions in the use of high-pressure sandblasting pipe: I. Pipe inner diameter: inner diameter of high-pressure sandblasting pipe. 2、 Attention shall be paid to the following items in the use and design of high-pressure sandblasting pipe: 1. The bending radius of high-pressure sandblasting pipe shall not be too small, and generally shall not be less than the value specified in the assembly technology of high-pressure sandblasting pipe. The joint between the high-pressure sandblasting pipe assembly and the pipe joint shall have a straight section, and its length shall not be less than twice the outer diameter of the pipe. 2. The length of high-pressure rubber hose assembly shall consider that the high-pressure rubber hose will shrink and deform after introducing pressure oil. Generally speaking, the shrinkage rate is 3~4 times of the pipe length. When installing the high-pressure rubber hose assembly, it is not allowed to bear tension. 3. During installation, the high-pressure sandblasting pipe assembly shall be free from torsional deformation. Air compression hose Price The connecting shaft of shall be placed in the moving plane as far as possible to avoid damaging the high-pressure sandblasting pipe when both ends move with each other. 4. High pressure resistant sand blasting pipe shall avoid contact and friction with mechanical sharp corners to avoid damaging the pipe. Safety measures: to ensure the safe and reliable use of high-pressure sandblasting pipe assembly.

Although fire CiH Air compression hose Explosion proof pipe) can be compressed and stretched, but if the installation position is incorrect, it will break quickly and reduce the service life. The sandblasting hose can be installed horizontally, vertically or obliquely. The most ideal condition is vertical installation. At the same time, avoid installing near the wheel, and install baffle if necessary. Generally speaking, the flame spraying metal sand blasting hose (explosion-proof pipe) can be divided into three lengths: the first is the compression length, that is, the length of the sand blasting hose when it is compressed to the limit position; The second is the installation length, that is, the length of the sandblasting hose when it is in the middle of half of the maximum displacement. The third type is the stretching length, that is, the length when the sandblasting hose is stretched to the maximum limit. When installing the sandblasting hose, the sandblasting hose should be in the middle position, which is called the installation length. When installed at this position, the sandblasting hose can move in two directions when bearing axial load. Otherwise, if it can only move in one direction, its strength will be affected and its service life will be reduced. In the actual installation process, considering that measuring the length of the sandblasting hose with a ruler according to the calculation results may affect the production efficiency, some foreign manufacturers directly install the ruler on the sandblasting hose, and cut the ruler after installation. From the structural point of view, the metal flame spraying metal sandblasting hose (explosion-proof pipe) is composed of strip and tube parts, which can form annular flame spraying metal sandblasting hose bellows and spiral flame spraying metal sandblasting hose bellows. Air compression hose Price Just because the corrugated pipe of the fire sprinkler metal sandblasting hose formed by this article always has a certain length of brazing or welding buckles and fire sprinkler metal sandblasting hose joints, the residues of the working medium often accumulate in these places, and the cleaning test and mechanical impurities in the working medium will deposit down to pollute the inner cavity. Therefore, its use reliability is relatively poor.