Whether in the process of purchase or use, production Oxygen tube The quality of all needs to be checked regularly. During the inspection, the following items should be noted. 1. Standard size and actual error of high-pressure rubber hose: because the inner diameter and outer diameter of high-pressure sand blasting pipe and the outer diameter of the skeleton layer will shake, if the shaking amplitude exceeds the allowable limit, the balance of the buckling amount of the sand blasting pipe joint cannot be guaranteed, and the quality of the sand blasting pipe assembly cannot be guaranteed. Therefore, for the sand blasting pipe selected for the production of sand blasting pipe assembly, it is necessary to strictly check whether the inner diameter and outer diameter of the skeleton layer meet the requirements, and the requirements for the outer diameter error can be appropriately relaxed. 2. Wall thickness error of high-pressure hose: due to the local pain of the rubber layer in the high-pressure sandblasting pipe and the influence of the overlapping width of the rubber layer of the high-pressure sandblasting pipe quality inspection center between the skeleton layers, the wall thickness error of the sandblasting pipe may be too large. If the wall thickness error exceeds the allowable range, it will affect the tightness and pull-out strength of the connector, and even cause some deflection (tilting head) of the hose assembly connector. Quality inspection of high-pressure sand blasting pipe Therefore, the wall thickness error of sand blasting pipe should be strictly controlled. Generally, the rubber hose with wall thickness error exceeding 0.5mm shall be selected stably. 3. Adhesion between each layer of high-pressure rubber hose: high-quality high-pressure sand blasting pipe shall have prominent integrity, that is, the quality inspection of high-pressure sand blasting pipe shall have high adhesion between each structural layer, and the adhesion between each adhesive layer shall become an integrity. Only in this way can we meet various technical requirements in the process of joint installation and fastening, and only in this way can we ensure the quality inspection requirements of high-pressure sand blasting pipes for sand blasting pipe assembly. Therefore, Oxygen tube Price It is necessary to control the adhesive force between each layer of the rubber hose not lower than that specified in the technical standard, and the rubber hose with high adhesive force shall be selected as far as possible to produce the rubber hose assembly.
Shaoxing production Oxygen tube Plays an important role. In the application of different industries, according to their own needs, check the performance of the products, give proper play to the advantages of the products, and ensure the normal use of daily applications. When replacing the wear-resistant sand blasting pipe, the length of the rubber pipe, the number of steel wire layers, the shape and size of the joint should be reasonable, and the curvature of the rubber pipe should be minimized. When tightening the connecting nuts, do not tighten the rubber hose. Excessive bending and twisting will greatly reduce the service life of the rubber hose. Protective measures shall be taken for the parts liable to friction to prevent the rubber hose from bursting due to wear. What should we pay attention to when purchasing wear-resistant sandblasting pipe? Different types of wear-resistant sand blasting pipes have different working pressures. When purchasing rubber hose, you should first determine the working pressure of the system, Oxygen tube Price Then select the equivalent working pressure of the hose. If the system is often affected by pressure, it is necessary to increase the working pressure of the hose and choose the hose with higher pulse life. The inner diameter of wear-resistant sand blasting pipe is one of the factors to be considered when selecting rubber hose. The small inner diameter will increase the flow rate of the medium, raise the temperature of the system, reduce the working efficiency, and affect the working performance of the system. The large inner diameter will increase the purchase cost. Therefore, the proper inner diameter should be selected according to the flow rate of the medium. The wear-resistant sand blasting pipe has allowable operating temperature range. The service life and pressure bearing capacity of the rubber pipe can be guaranteed only when it works at an appropriate temperature. When the operating temperature of the equipment exceeds the allowable temperature range of the rubber hose for a long time, special rubber hose shall be purchased or special protective sleeve shall be added on the wear-resistant sand blasting pipe. If the medium to be transported is special, make sure that the hose material is compatible with the medium.
production Oxygen tube 1. During the molding of rubber products, the cohesive force of the elastomer cannot be eliminated due to the large pressure pressing. During the molding and mold release, extremely unstable shrinkage (the shrinkage rate of rubber varies due to different rubber types) often occurs. It must take a period of time before it can be gentle and stable. Therefore, at the beginning of the design of a rubber product, no matter the formula or the mold, it is necessary to carefully calculate the matching. If not, it is easy to cause dimensional instability of the product, resulting in low product quality. 2. Rubber belongs to thermosetting elastomer, while plastic belongs to thermosetting elastomer. Due to different sulfide types, the temperature range of rubber molding and curing is quite different, even affected by climate change and indoor temperature and humidity. Therefore, the production conditions of rubber products need to be properly adjusted at any time. If not, there may be differences in product quality. 3. The rubber product is the rubber mixture made from rubber raw materials after mixing in the internal mixer as the raw material. The formula is designed according to the characteristics of the required rubber products during mixing, and the required product hardness is determined. The product is molded by the rubber plate vulcanizer. After the product is formed, flash processing shall be carried out to make the product surface smooth without burrs. 4. The aging test of rubber products belongs to the category of aging test. Rubber aging refers to the phenomenon that the performance and structure of rubber and products are changed due to the combined effect of internal and external factors in the process of processing, storage and use, thus losing their use value. Oxygen tube Price It is characterized by cracking, tackiness, hardening, softening, chalking, discoloration, mildew, etc. The following conditions shall be met when the ball mill uses the rubber lining plate: 1. The hardness of the ground material. The iron base alloy is similar to the rubber lining plate for materials below medium hardness, and the rubber lining plate is superior for materials above medium hardness. 2. The temperature of rubber lining plate is generally 70 ℃ - 90 ℃, and it can reach 110-130 ℃ under special circumstances. The temperature should be lower during dry grinding. 3. Feed size. Generally, the ball mill shall be more than 20-25mm; For the autogenous mill, the feeding particle size can be larger because no steel ball is added.
In the shipbuilding industry, radio industry, electrical industry, telecommunications industry, instrument industry, aviation industry, medical industry, etc., we often see acid and alkali resistant hose, then what is Shaoxing Oxygen tube What about? If you want to know more, please read down! Acid and alkali resistant silicone hose is a kind of pipe specially used for power equipment, which uses acid and alkali resistant silica gel as the main raw material and tightly wraps the pipe wall with electrical grade polyethylene spiral wire. Due to the chemical inertia of acid and alkali resistant silica gel, this kind of pipe has good acid and alkali resistance performance and electrical performance, and is commonly used in the production of wires, cables and lead wires in extreme acid and alkali environments. Also called: acid and alkali resistant silicone rubber hose, acid and alkali resistant silicone rubber hose, acid and alkali resistant silicone rubber hose, acid and alkali resistant silicone rubber hose, acid and alkali resistant silicone rubber hose. Features: 1. High temperature resistance (250-300 ℃) and low temperature resistance (- 40-60 ℃); 2. Good acid and alkali resistance. Physiologically stable, able to withstand repeated harsh and disinfection conditions, resistant to ozone aging, light aging, weather aging and ultraviolet radiation. 3. Small resilience and permanent deformation (no more than 50% at 200 ℃ for 48 hours), breakdown voltage (20-25KV/mm), ozone resistance and UV resistance. Oxygen tube Price Radiation resistance and other characteristics, 4. Good electrical performance, small change when exposed to moisture, water or temperature rise, even if the silica generated by short circuit combustion is still an insulator, which ensures that electrical equipment continues to work, so it is most suitable for making wires, cables and lead wires.
Prof. Weina, University of New South Wales, Australia? Sahajwara has developed a new method of using waste rubber and plastic for steel production - polymer injection process. Shaoxing Oxygen tube It can not only greatly reduce the environmental pollution caused by waste rubber and waste plastics, but also effectively reduce the cost of steel production. Waste rubber and plastic contain a lot of carbon. Waste rubber and plastic are put into the electric arc furnace as substitutes for carbon element. The carbon originally locked in the waste plastic hose will react at ultra-high temperature and burn with coal to become clean fuel, thus reducing greenhouse gas emissions, At the same time, it also alleviates the environmental pollution caused by using them as landfill. The advantage of polymer injection process is that by injecting polymer and coke or anthracite rubber tube mixture, the volume of slag can be increased and the foaming degree can be increased, which can extend the arc length, increase the heat transfer from the arc to steel, reduce the heat loss through the slag and side walls, and thus improve the power efficiency. This reduces power consumption by about 3%. For every 1 ton of steel, about 24% of the cost comes from the cost of electricity. After polymer injection technology is adopted, each furnace of steel is, Oxygen tube Price The average total amount of carbon injected can be reduced by 10%~20%. In addition, the potential price of polymer is lower than that of coke, and the total cost of carbon injection can be saved by 15%~35%.