Acid and alkali resistant pipe company It has become the standard configuration of the modern new ball mill, but many problems may occur during the use or installation of the rubber lining plate, which will cause the failure of the rubber lining plate of the ball mill. Here is a brief introduction to the causes of the more common failure of the rubber lining plate of the ball mill. The design and installation are not professional and reasonable. The design and installation are also common problems for many novice manufacturers. For example, the bolt holes for fixing the ball mill lining plate are square, which will cause stress concentration and fracture. Adjust the size of lining plate to control the gap between lining plates at about 8mm; The installation quality of lining plate is very important to the safe operation of ball mill. First, tighten the fixed wedge symmetrically, put the lining plate in sequence, and then use the tightening wedge to secure it; Therefore, professional installation guidance can easily avoid these problems. The reason why the rubber lining plate of the ball mill does not match the steel ball is relatively common, and it is easy for many novice manufacturers to ignore and make mistakes. During the operation of the ball mill, the rubber lining plate of the ball mill, materials and steel balls promote the normal grinding and crushing of the ball mill due to the interaction of forces. The hardness of materials is related to wear resistance, and the wear resistance increases with the increase of hardness, Huanggang Acid and alkali resistant pipe It is a pair of friction pairs, and the increase of hardness of one side will cause the wear of the other side to increase. Therefore, the high wear-resistant rubber lining plate is matched with the high wear-resistant steel ball, and the low wear-resistant rubber lining plate is matched with the low wear-resistant steel ball, so as to ensure the normal wear of the rubber lining plate of the ball mill and extend the service life of the ball mill.

As high quality Acid and alkali resistant pipe As an important part of sand blasting machinery, its safety plays a vital role in the safety of equipment operation. The following will briefly analyze the precautions in the use of high-pressure sandblasting pipe: I. Pipe inner diameter: inner diameter of high-pressure sandblasting pipe. 2、 Attention shall be paid to the following items in the use and design of high-pressure sandblasting pipe: 1. The bending radius of high-pressure sandblasting pipe shall not be too small, and generally shall not be less than the value specified in the assembly technology of high-pressure sandblasting pipe. The joint between the high-pressure sandblasting pipe assembly and the pipe joint shall have a straight section, and its length shall not be less than twice the outer diameter of the pipe. 2. The length of high-pressure rubber hose assembly shall consider that the high-pressure rubber hose will shrink and deform after introducing pressure oil. Generally speaking, the shrinkage rate is 3~4 times of the pipe length. When installing the high-pressure rubber hose assembly, it is not allowed to bear tension. 3. During installation, the high-pressure sandblasting pipe assembly shall be free from torsional deformation. Acid and alkali resistant pipe company The connecting shaft of shall be placed in the moving plane as far as possible to avoid damaging the high-pressure sandblasting pipe when both ends move with each other. 4. High pressure resistant sand blasting pipe shall avoid contact and friction with mechanical sharp corners to avoid damaging the pipe. Safety measures: to ensure the safe and reliable use of high-pressure sandblasting pipe assembly.

high quality Acid and alkali resistant pipe 1. During the molding of rubber products, the cohesive force of the elastomer cannot be eliminated due to the large pressure pressing. During the molding and mold release, extremely unstable shrinkage (the shrinkage rate of rubber varies due to different rubber types) often occurs. It must take a period of time before it can be gentle and stable. Therefore, at the beginning of the design of a rubber product, no matter the formula or the mold, it is necessary to carefully calculate the matching. If not, it is easy to cause dimensional instability of the product, resulting in low product quality. 2. Rubber belongs to thermosetting elastomer, while plastic belongs to thermosetting elastomer. Due to different sulfide types, the temperature range of rubber molding and curing is quite different, even affected by climate change and indoor temperature and humidity. Therefore, the production conditions of rubber products need to be properly adjusted at any time. If not, there may be differences in product quality. 3. The rubber product is the rubber mixture made from rubber raw materials after mixing in the internal mixer as the raw material. The formula is designed according to the characteristics of the required rubber products during mixing, and the required product hardness is determined. The product is molded by the rubber plate vulcanizer. After the product is formed, flash processing shall be carried out to make the product surface smooth without burrs. 4. The aging test of rubber products belongs to the category of aging test. Rubber aging refers to the phenomenon that the performance and structure of rubber and products are changed due to the combined effect of internal and external factors in the process of processing, storage and use, thus losing their use value. Acid and alkali resistant pipe company It is characterized by cracking, tackiness, hardening, softening, chalking, discoloration, mildew, etc. The following conditions shall be met when the ball mill uses the rubber lining plate: 1. The hardness of the ground material. The iron base alloy is similar to the rubber lining plate for materials below medium hardness, and the rubber lining plate is superior for materials above medium hardness. 2. The temperature of rubber lining plate is generally 70 ℃ - 90 ℃, and it can reach 110-130 ℃ under special circumstances. The temperature should be lower during dry grinding. 3. Feed size. Generally, the ball mill shall be more than 20-25mm; For the autogenous mill, the feeding particle size can be larger because no steel ball is added.

I believe everyone is familiar with high quality Acid and alkali resistant pipe Relevant application knowledge of products. It is understood that at present, this product is mainly used for mining hydraulic support and oilfield development. It is applicable to engineering construction, lifting transportation, metallurgical forging, mining equipment, ships, injection molding machinery, agricultural machinery, various machine tools, mechanization of various industrial departments, water-based liquids, etc. And liquid transmission. Its relatively high working pressure can reach 70-120 MPa. In order to achieve better application effect, what problems should be paid attention to when using high-pressure braided hose? 1. The bending radius shall not be less than the given bending radius to prevent damage to the hose skeleton or premature failure due to excessive tension. 2. Select the type and specification of the hose correctly according to the use conditions, and do not misuse or replace it. 3. When using high-pressure braided hose, the pressure should be adjusted slowly and evenly to avoid sudden pressure increase and damage to the pipe body. 4. When the work site changes, it should be removed from the ground without dragging, so as to avoid the skeleton layer being corroded after scratching the outer glue. 5. After delivering corrosive liquid, the interior should be cleaned to prevent residues from corroding the pipe body for a long time, or select corresponding series of products. When storing high-pressure braided rubber hoses, depending on the type of rubber used, Acid and alkali resistant pipe company Note which conditions typically change over time. However, due to several factors or a combination of several factors, this change may accelerate, and other materials used to strengthen high-pressure braided hoses may also be adversely affected by improper storage conditions.