Wear resistant hose company It has become the standard configuration of the modern new ball mill, but many problems may occur during the use or installation of the rubber lining plate, which will cause the failure of the rubber lining plate of the ball mill. Here is a brief introduction to the causes of the more common failure of the rubber lining plate of the ball mill. The design and installation are not professional and reasonable. The design and installation are also common problems for many novice manufacturers. For example, the bolt holes for fixing the ball mill lining plate are square, which will cause stress concentration and fracture. Adjust the size of lining plate to control the gap between lining plates at about 8mm; The installation quality of lining plate is very important to the safe operation of ball mill. First, tighten the fixed wedge symmetrically, put the lining plate in sequence, and then use the tightening wedge to secure it; Therefore, professional installation guidance can easily avoid these problems. The reason why the rubber lining plate of the ball mill does not match the steel ball is relatively common, and it is easy for many novice manufacturers to ignore and make mistakes. During the operation of the ball mill, the rubber lining plate of the ball mill, materials and steel balls promote the normal grinding and crushing of the ball mill due to the interaction of forces. The hardness of materials is related to wear resistance, and the wear resistance increases with the increase of hardness, Taiyuan Wear resistant hose It is a pair of friction pairs, and the increase of hardness of one side will cause the wear of the other side to increase. Therefore, the high wear-resistant rubber lining plate is matched with the high wear-resistant steel ball, and the low wear-resistant rubber lining plate is matched with the low wear-resistant steel ball, so as to ensure the normal wear of the rubber lining plate of the ball mill and extend the service life of the ball mill.

Taiyuan Wear resistant hose It is used for transportation, construction and other operating equipment. Incorrect operation and incorrect environment may affect the normal use of steel braided sandblasting pipe. What specific factors will affect the normal use of steel braided sand blasting pipe? The quality will definitely affect the use effect. The poor quality is actually related to the selected raw materials. Some raw materials are of high quality, and the quality of steel braided sandblasting pipes produced is also very good. However, if the steel braided sand blasting pipe is made of inferior plastic, the quality is very poor, which also affects the use effect. The use environment affects the use effect. Anti static steel braided sand blasting pipe is usually used in industry. Because these products are very common, the demand is also large. However, people do not pay attention to the use environment. If used in strong acid and alkali environment, steel braided sand blasting pipe will naturally corrode. Or if used in a relatively high temperature area, the steel braided sandblasting pipe may melt. Anti static steel braided sand blasting pipe will also affect the use effect. In the eyes of most users, the greater the degree, the better the nature. So if you choose a good one, users can use it with confidence. Understanding and avoiding the wrong use of high-pressure pipeline can reduce the possibility of high-pressure pipeline failure. The following brief introduction will help you. 1. Frequent and serious pressure shock: high-pressure pipeline burst is generally not caused by excessive static pressure, but is related to the severity and frequency of pressure shock. During the operation of construction machinery, the sudden increase or decrease of oil pressure in the high-pressure pipe will occur repeatedly, which will cause frequent pressure shocks to the oil pipe, leading to the aggravation of oil seal damage at various parts, blistering and cracking of rubber hose, and loosening and leakage of pipe joints. Therefore, during operation, the valve rod shall not be pulled too hard, but must be pulled gently. 2. The use temperature of oil is too high: during the operation of construction machinery, due to the power loss of the hydraulic system, the oil will rise, and the external temperature (especially in summer) will lead to a sharp rise in the oil temperature. high quality Wear resistant hose company The higher the oil temperature is, the easier the rubber is to age, the worse the elasticity is, the lower the strength and sealing performance are, and the high-pressure pipe will burst rapidly. Therefore, when the temperature rise of the hydraulic system is too high or too fast during operation, the causes should be found out and eliminated in time. For summer operation, especially continuous operation, necessary cooling measures shall be taken.

one Taiyuan Wear resistant hose When using, the talcum powder on the inner wall of the hose must be blown clean to prevent the channel of the welding torch from being blocked. Avoid external extrusion and mechanical damage during use, and do not fold the pipe body. 2. Care must be taken when storing and using the hose to keep it clean and free from damage. For example, avoid exposure to sunlight, rain and snow, and prevent contact with acids, alkalis, oils and other organic solvents that can damage the hose. The storage temperature shall be - 15~40 ℃, and the distance from the heat source shall not be less than 1m. 3. According to the national standards, the oxygen hose is red, the working pressure vessel is 1.5MPa, the inner diameter of the hose is 8mm, and the outer diameter is 18mm; The acetylene hose is black, the working pressure vessel is 0.3MPa, the inner diameter of the hose is 8mm, and the outer diameter is 16mm. 4. The gas cutting operation requires a large oxygen output, so the valves of the gas cylinder (or oxygen pipeline) connected to the high pressure end of the oxygen meter should be fully opened to ensure adequate flow and stable pressure. The low pressure gauge has indicated the working pressure, but the pressure drops suddenly when using oxygen. At this time, it is easy to backfire and may backfire into the oxygen hose to cause explosion. 5. Oxygen hose and acetylene hose shall not be mixed or substituted with each other, and oxygen and hose shall not be used to blow away the blockage of acetylene hose. At the same time, it is necessary to check and eliminate the defects such as gas leakage and blockage of the welding torch at any time to prevent the formation of oxygen and acetylene mixture in the hose. It should be pointed out that the hose color specified in the national standard is opposite to that specified in the international standard (ISO) (oxygen hose is black, acetylene hose is red). At the same time, it is different from the original ministerial standard (HG4-605-66) that oxygen hose is red and acetylene hose is green. Before 1966, domestic oxygen hose was black or green and acetylene hose was red. thus Wear resistant hose company It causes inconsistency between the understanding and habits of the supply department and the user, and is easy to cause accidents due to the mixing and substitution of rubber hoses. At present, it should be emphasized that unified understanding and use should be carried out in accordance with the provisions of national standards, and attention should be paid to distinguishing the rubber hoses of imported equipment.

Although fire Taiyuan Wear resistant hose Explosion proof pipe) can be compressed and stretched, but if the installation position is incorrect, it will break quickly and reduce the service life. The sandblasting hose can be installed horizontally, vertically or obliquely. The most ideal condition is vertical installation. At the same time, avoid installing near the wheel, and install baffle if necessary. Generally speaking, the flame spraying metal sand blasting hose (explosion-proof pipe) can be divided into three lengths: the first is the compression length, that is, the length of the sand blasting hose when it is compressed to the limit position; The second is the installation length, that is, the length of the sandblasting hose when it is in the middle of half of the maximum displacement. The third type is the stretching length, that is, the length when the sandblasting hose is stretched to the maximum limit. When installing the sandblasting hose, the sandblasting hose should be in the middle position, which is called the installation length. When installed at this position, the sandblasting hose can move in two directions when bearing axial load. Otherwise, if it can only move in one direction, its strength will be affected and its service life will be reduced. In the actual installation process, considering that measuring the length of the sandblasting hose with a ruler according to the calculation results may affect the production efficiency, some foreign manufacturers directly install the ruler on the sandblasting hose, and cut the ruler after installation. From the structural point of view, the metal flame spraying metal sandblasting hose (explosion-proof pipe) is composed of strip and tube parts, which can form annular flame spraying metal sandblasting hose bellows and spiral flame spraying metal sandblasting hose bellows. Wear resistant hose company Just because the corrugated pipe of the fire sprinkler metal sandblasting hose formed by this article always has a certain length of brazing or welding buckles and fire sprinkler metal sandblasting hose joints, the residues of the working medium often accumulate in these places, and the cleaning test and mechanical impurities in the working medium will deposit down to pollute the inner cavity. Therefore, its use reliability is relatively poor.

Taiyuan Wear resistant hose Vulcanization of technical performance indicators is an important process to enhance the adhesive strength between rubber and reinforcement layer and make it a whole in rubber hose manufacturing, and also an important link to ensure and improve product quality. In order to obtain good pulse performance and service performance of steel wire reinforced rubber hose, in addition to reasonable structure and formula, it is necessary to ensure the compactness of vulcanized hose. In order to meet this performance requirement, the traditional vulcanization method is to wrap the water in water cloth on the semi-finished hose before vulcanization, make braided hose or steel wire for reinforcement and fastening, and vulcanize in batches with steam vulcanization tank. Since the performance requirements of medium and low pressure hoses are low, the rubber hose can also be directly put into the curing tank without fastening. Although water wrapped cloth vulcanization can also increase the compactness of the hose, its appearance is poor. In order to obtain the smooth outer surface of the hose, the lead coating vulcanization method is widely used at home and abroad. For decades, people have been using this method as an effective method to vulcanize and strengthen rubber hoses, especially high-pressure rubber hoses. So far, many domestic and foreign manufacturers are still using this method to produce rubber hoses. But the fatal disadvantage of this method is that it pollutes the environment. Wear resistant hose company The main control function of the air compressor station unit is to exhaust more air. According to different structures, it can be divided into full hose, cloth hose, steel braided hose, etc. According to different uses, it can be divided into air hose, water suction hose, water delivery hose, heat resistant hose, acid (alkali) resistant hose, oil resistant hose and special hose., It can be closed within the specified range.

Due to the limitation of spatial location conditions, high quality Wear resistant hose The installation stress of can often bring various difficulties to the installation work: formed pipes cannot be installed; When you bend down, you are about to come. If you make do with pipes, local cold correction will inevitably occur. According to the size of the pipeline and the specific situation on site, the cold correction amount varies from several millimeters to tens of millimeters, some as high as hundreds of millimeters. Practice has proved that the greater the quantity, the higher the internal stress. These residual installation stresses in the rubber sand blasting pipe are undoubtedly huge hidden information. The lubricating oil duct of a certain type of engine bearing was broken for many times due to excessive installation stress in actual operation. Because it can be bent at will, the internal stress generated by bending under the condition of rated bending radius is very small, which brings great convenience to the installation work, and also plays a certain role in ensuring the safe operation of the rubber sand blasting pipe. This is the main reason why some rubber sand blasting pipes must be used. Since it is necessary to load and unload the mold, the movable cylinder on the vulcanizer will move up and down. After repeated reciprocation, the copper serpentine tube will undergo fatigue fracture. Although it can continue to be used after repair, stopping for repair will cause time loss. Taiyuan Wear resistant hose Although it has good flexibility and strong fatigue resistance, it is also weak in pressure bearing, temperature resistance, aging resistance and other aspects, and can not be used after several months. The good comprehensive performance of rubber sand blasting pipe is fully reflected here.