Whether in the process of purchase or use, high quality Rubber steel wire pipe The quality of all needs to be checked regularly. During the inspection, the following items should be noted. 1. Standard size and actual error of high-pressure rubber hose: because the inner diameter and outer diameter of high-pressure sand blasting pipe and the outer diameter of the skeleton layer will shake, if the shaking amplitude exceeds the allowable limit, the balance of the buckling amount of the sand blasting pipe joint cannot be guaranteed, and the quality of the sand blasting pipe assembly cannot be guaranteed. Therefore, for the sand blasting pipe selected for the production of sand blasting pipe assembly, it is necessary to strictly check whether the inner diameter and outer diameter of the skeleton layer meet the requirements, and the requirements for the outer diameter error can be appropriately relaxed. 2. Wall thickness error of high-pressure hose: due to the local pain of the rubber layer in the high-pressure sandblasting pipe and the influence of the overlapping width of the rubber layer in the high-pressure sandblasting pipe quality inspection center between the skeleton layers, the wall thickness error of the sandblasting pipe may be too large. If the wall thickness error exceeds the allowable range, it will affect the tightness and pull-out strength of the connector, and even cause some deflection (tilting head) of the hose assembly connector. Quality inspection of high-pressure sand blasting pipe Therefore, the wall thickness error of sand blasting pipe should be strictly controlled. Generally, the rubber hose with wall thickness error exceeding 0.5mm shall be selected stably. 3. Adhesion between each layer of high-pressure rubber hose: high-quality high-pressure sand blasting pipe shall have prominent integrity, that is, the quality inspection of high-pressure sand blasting pipe shall have high adhesion between each structural layer, and the adhesion between each adhesive layer shall become an integrity. Only in this way can we meet various technical requirements in the process of joint installation and fastening, and only in this way can we ensure the quality inspection requirements of high-pressure sand blasting pipes for sand blasting pipe assembly. Therefore, Rubber steel wire pipe company It is necessary to control the adhesive force between each layer of the rubber hose not lower than that specified in the technical standard, and the rubber hose with high adhesive force shall be selected as far as possible to produce the rubber hose assembly.
Haikou Rubber steel wire pipe Structure type of product: sand blasting hose is mainly composed of liquid resistant inner rubber layer, middle rubber layer, 2 or 4 or 6 layers of steel wire winding reinforcement layer and outer rubber layer. The inner rubber layer has the function of bearing the pressure of the transmission medium and protecting the steel wire from erosion, the outer rubber layer protects the steel wire from damage, and the steel wire (0.3-2.0 steel wire) layer is the reinforced skeleton material. Application of sandblasting hose products: high-pressure sandblasting hose is mainly used for mining hydraulic support and oil field exploitation, and is suitable for engineering construction, lifting and transportation, metallurgical forging, mining equipment, ships, injection molding machinery, agricultural machinery, various machine tools, and mechanical and automatic hydraulic systems in various industrial sectors to transport petroleum base with a certain pressure (higher pressure) and temperature. (such as mineral oil, soluble oil, hydraulic oil, fuel oil, lubricating oil) and water-based liquid (such as emulsion, oil-water emulsion, water). And liquid transmission. The working withstand voltage can reach 70-100 MPa. The company's sand blasting hose standards refer to national standards/T10544-03, DIN 20023, and SaE100 R9-13. Rubber steel wire pipe company Made of special synthetic rubber, it has excellent oil resistance, heat resistance and aging resistance. The rubber hose has high bearing pressure and superior pulse performance. The tube body is tightly combined, soft to use, and has little compression deformation. The hose has excellent bending resistance and fatigue resistance. The sandblasting hose is 20m long and can be made within 50m as required.
high quality Rubber steel wire pipe 1. During the molding of rubber products, the cohesive force of the elastomer cannot be eliminated due to the large pressure pressing. During the molding and mold release, extremely unstable shrinkage (the shrinkage rate of rubber varies due to different rubber types) often occurs. It must take a period of time before it can be gentle and stable. Therefore, at the beginning of the design of a rubber product, no matter the formula or the mold, it is necessary to carefully calculate the matching. If not, it is easy to cause dimensional instability of the product, resulting in low product quality. 2. Rubber belongs to thermosetting elastomer, while plastic belongs to thermosetting elastomer. Due to different sulfide types, the temperature range of rubber molding and curing is quite different, even affected by climate change and indoor temperature and humidity. Therefore, the production conditions of rubber products need to be properly adjusted at any time. If not, there may be differences in product quality. 3. The rubber product is the rubber mixture made from rubber raw materials after mixing in the internal mixer as the raw material. The formula is designed according to the characteristics of the required rubber products during mixing, and the required product hardness is determined. The product is molded by the rubber plate vulcanizer. After the product is formed, flash processing shall be carried out to make the product surface smooth without burrs. 4. The aging test of rubber products belongs to the category of aging test. Rubber aging refers to the phenomenon that the performance and structure of rubber and products are changed due to the combined effect of internal and external factors in the process of processing, storage and use, thus losing their use value. Rubber steel wire pipe company It is characterized by cracking, tackiness, hardening, softening, chalking, discoloration, mildew, etc. The following conditions shall be met when the ball mill uses the rubber lining plate: 1. The hardness of the ground material. The iron base alloy is similar to the rubber lining plate for materials below medium hardness, and the rubber lining plate is superior for materials above medium hardness. 2. The temperature of rubber lining plate is generally 70 ℃ - 90 ℃, and it can reach 110-130 ℃ under special circumstances. The temperature should be lower during dry grinding. 3. Feed size. Generally, the ball mill shall be more than 20-25mm; For the autogenous mill, the feeding particle size can be larger because no steel ball is added.
one Haikou Rubber steel wire pipe When using, the talcum powder on the inner wall of the hose must be blown clean to prevent the channel of the welding torch from being blocked. Avoid external extrusion and mechanical damage during use, and do not fold the pipe body. 2. Care must be taken when storing and using the hose to keep it clean and free from damage. For example, avoid exposure to sunlight, rain and snow, and prevent contact with acids, alkalis, oils and other organic solvents that can damage the hose. The storage temperature shall be - 15~40 ℃, and the distance from the heat source shall not be less than 1m. 3. According to the national standards, the oxygen hose is red, the working pressure vessel is 1.5MPa, the inner diameter of the hose is 8mm, and the outer diameter is 18mm; The acetylene hose is black, the working pressure vessel is 0.3MPa, the inner diameter of the hose is 8mm, and the outer diameter is 16mm. 4. The gas cutting operation requires a large oxygen output, so the valves of the gas cylinder (or oxygen pipeline) connected to the high pressure end of the oxygen meter should be fully opened to ensure adequate flow and stable pressure. The low pressure gauge has indicated the working pressure, but the pressure drops suddenly when using oxygen. At this time, it is easy to backfire and may backfire into the oxygen hose to cause explosion. 5. Oxygen hose and acetylene hose shall not be mixed or substituted with each other, and oxygen and hose shall not be used to blow away the blockage of acetylene hose. At the same time, it is necessary to check and eliminate the defects such as gas leakage and blockage of the welding torch at any time to prevent the formation of oxygen and acetylene mixture in the hose. It should be pointed out that the hose color specified in the national standard is opposite to that specified in the international standard (ISO) (oxygen hose is black, acetylene hose is red). At the same time, it is different from the original ministerial standard (HG4-605-66) that oxygen hose is red and acetylene hose is green. Before 1966, domestic oxygen hose was black or green and acetylene hose was red. thus Rubber steel wire pipe company It causes inconsistency between the understanding and habits of the supply department and the user, and is easy to cause accidents due to the mixing and substitution of rubber hoses. At present, it should be emphasized that unified understanding and use should be carried out in accordance with the provisions of national standards, and attention should be paid to distinguishing the rubber hoses of imported equipment.
