high quality Cord hose It will burst for a long time due to frequent and severe pressure shocks. This situation is usually not caused by excessive static pressure, but is related to the strength and frequency of pressure shock. During the operation of construction machinery, the oil pressure in the oil resistant hose will rise or fall repeatedly, and then it will form frequent pressure shocks to the oil pipe, causing the oil seal of each part to become more damaged, the oil resistant hose will bubble and break, and the pipe joint will become loose and leak. Therefore, in the process of operation, the valve rod should not be pulled too hard, and it needs to be gentle. The application temperature of the oil in the oil resistant rubber hose is too high, resulting in aging and bursting of the rubber hose. During the operation of construction machinery, the hydraulic system will cause the oil to become hot due to power failure, and the influence of external temperature (especially in summer) will cause the oil temperature to rise sharply. The higher the oiling temperature is, the easier the rubber hose ages, the worse the elasticity is, the lower the strength and sealing function are, and the oil resistant hose will burst quickly. Therefore, Cord hose company During operation, when the temperature rise of the hydraulic system is too high or too fast, the causes should be found and eliminated in time. Necessary cooling measures shall be taken for summer operation, especially continuous operation.

1. The use of protection cannot be ignored: the long-term use of high-pressure sand blasting hose joints at home usually does not cause concern, but excessive use and improper protection also buried the hidden danger of joint cracking to a certain extent. It is understood that the service life of the joint is usually 200000 times, and it should be replaced after long-term use. When using the side, Cord hose company Care should be taken to close and open as gently as possible and not to rotate the knob of the hose connector repeatedly. 2. Differentiation of quality can be based on standard evidence collection. It is understood that it is still difficult to determine the cause of joint cracking. At present, the National Bureau of Technology and Quality Supervision has issued recommendations for sealing nozzles and hose specifications. These two specifications perfectly adjust the quality specification target of connectors and hoses. Consumers can go to the quality inspection department to check the torsional strength of the connecting hose, the tightness of the connecting spool and the strength of the connecting materials. If the content of standard rules cannot be met, it will be attributed to quality problems, which can serve as a strong basis for expression. 3. The appearance of hose connector is difficult to distinguish between good and bad. In order to pursue profits and reduce costs, many manufacturers currently use selected cast iron (easy to rust) and zinc alloy (non anti-corrosion) as materials to produce high-pressure sand blasting hose joints, which causes product quality problems. It is understood that the quality of connectors and hoses is not up to standard, Lanzhou Cord hose The strength function and sealing function of high-pressure sand blasting hose joints are not up to standard due to problems such as materials and wall thickness, which should be paid attention to by consumers.

Lanzhou Cord hose Structure type of product: sand blasting hose is mainly composed of liquid resistant inner rubber layer, middle rubber layer, 2 or 4 or 6 layers of steel wire winding reinforcement layer and outer rubber layer. The inner rubber layer has the function of bearing the pressure of the transmission medium and protecting the steel wire from erosion, the outer rubber layer protects the steel wire from damage, and the steel wire (0.3-2.0 steel wire) layer is the reinforced skeleton material. Application of sandblasting hose products: high-pressure sandblasting hose is mainly used for mining hydraulic support and oil field exploitation, and is suitable for engineering construction, lifting and transportation, metallurgical forging, mining equipment, ships, injection molding machinery, agricultural machinery, various machine tools, and mechanical and automatic hydraulic systems in various industrial sectors to transport petroleum base with a certain pressure (higher pressure) and temperature. (such as mineral oil, soluble oil, hydraulic oil, fuel oil, lubricating oil) and water-based liquid (such as emulsion, oil-water emulsion, water). And liquid transmission. The working withstand voltage can reach 70-100 MPa. The company's sand blasting hose standards refer to national standards/T10544-03, DIN 20023, and SaE100 R9-13. Cord hose company Made of special synthetic rubber, it has excellent oil resistance, heat resistance and aging resistance. The rubber hose has high bearing pressure and superior pulse performance. The tube body is tightly combined, soft to use, and has little compression deformation. The hose has excellent bending resistance and fatigue resistance. The sandblasting hose is 20m long and can be made within 50m as required.

Cord hose company It has become the standard configuration of the modern new ball mill, but many problems may occur during the use or installation of the rubber lining plate, which will cause the failure of the rubber lining plate of the ball mill. Here is a brief introduction to the causes of the more common failure of the rubber lining plate of the ball mill. The design and installation are not professional and reasonable. The design and installation are also common problems for many novice manufacturers. For example, the bolt holes for fixing the ball mill lining plate are square, which will cause stress concentration and fracture. Adjust the size of lining plate to control the gap between lining plates at about 8mm; The installation quality of lining plate is very important to the safe operation of ball mill. First, tighten the fixed wedge symmetrically, put the lining plate in sequence, and then use the tightening wedge to secure it; Therefore, professional installation guidance can easily avoid these problems. The reason why the rubber lining plate of the ball mill does not match the steel ball is relatively common, and it is easy for many novice manufacturers to ignore and make mistakes. During the operation of the ball mill, the rubber lining plate of the ball mill, materials and steel balls promote the normal grinding and crushing of the ball mill due to the interaction of forces. The hardness of materials is related to wear resistance, and the wear resistance increases with the increase of hardness, Lanzhou Cord hose It is a pair of friction pairs, and the increase of hardness of one side will cause the wear of the other side to increase. Therefore, the high wear-resistant rubber lining plate is matched with the high wear-resistant steel ball, and the low wear-resistant rubber lining plate is matched with the low wear-resistant steel ball, so as to ensure the normal wear of the rubber lining plate of the ball mill and extend the service life of the ball mill.