The hard core method adopts the core extrusion process to extrude the inner rubber tube blank, which directly uses the extruder to cover the inner rubber tube blank on the iron core, instead of the traditional casing process, and simplifies the process flow. Lanzhou Sandblasting hose The billet forming adopts the process method of intertwining outer film and steel wire braiding forming. Similar to wrapping water wrapped cloth, the overlapping width is 1/2 of the film width. This process method can replace the method of wrapping outer film by extruder or by hand, reducing energy consumption and cost. We all know that the reinforcing layer and reinforcing layer of the rubber hose are the main force bearing parts, which are used to bear the load pressure. The factors determining the stress condition of the reinforced layer of the rubber hose are determined by the tension of the braided steel wire and the braiding angle. The high-speed steel wire hose braiding machine developed by our factory has introduced the advanced technology of foreign braiding production lines, and integrated the characteristics of domestic braiding machines. It integrates the advanced functions of hydraulic brake hose braiding production line, such as horizontal mechanical transmission, automatic lubrication, and so on, to develop equipment with high productivity and high degree of automation. The range of braiding diameter can be achieved Ф 6— Ф 25 Long core rubber hose (reinforcement layer). It fills the gap of domestic knitting production equipment, which can be widely used in rubber and plastic hose, rubber hose (reinforcement layer) knitting production equipment. The structure of high-pressure rubber hose is composed of four parts: inner liner, inner rubber layer, skeleton layer, middle rubber layer and outer rubber layer. Sandblasting hose Where can I find it? In case of direct contact with the conveying medium, the synthetic rubber with good medium resistance, high tensile strength, high constant tensile stress, small compression permanent deformation and easy processing is usually selected. In order to meet the use requirements of strong polar medium resistance, the inner liner is composed of polytetrafluoroethylene layer and rubber layer, and a layer of film or adhesive is added on the surface of the inner liner to improve the adhesion with the skeleton material.

Lanzhou wear-resisting In places that must be crossed or may rub with the mechanical surface when working, hose clamps or springs and other protective devices should be used to prevent the outer layer of the sandblasting hose from being damaged. Sand blasting hose shall be arranged to avoid heat source as far as possible and away from the performance of engine exhaust pipe. If necessary, sleeve or protective screen can be used to prevent the hose from being heated and deteriorated. When the sand blasting hose must be bent, the bending radius should not be too small, and should be greater than 9 times the outer diameter. There should be a straight line section greater than 2 times the outer diameter of the pipe at the joint between the rubber hose and the joint. How high-quality the products and equipment we use are, it is inevitable that there will be some large and small failures in the process of using them, which will more or less have a certain impact on our work. Just like the use of sandblasting hose, there are traces of its outer adhesive seam, problems must be solved, For this, we explained the following solutions: First, the used water cloth should be used according to the original elastic edge of the water cloth when it is reused. 2： When we wrap the water cloth around the seam of the sandblasting hose, we should apply sufficient and uniform pressure to the pipe body. 3. The water cloth with different widths should be selected according to the size of the outer diameter of the wrapped sandblasting hose (for hose with an outer diameter of less than 30mm, the width of the water cloth should not exceed 90mm). The overlapping width of the water cloth should be 3/5-2/3 of the width of the water cloth.

Whether in the process of purchase or use, wear-resisting Sandblasting hose The quality of all needs to be checked regularly. During the inspection, the following items should be noted. 1. Standard size and actual error of high-pressure rubber hose: because the inner diameter and outer diameter of high-pressure sand blasting pipe and the outer diameter of the skeleton layer will shake, if the shaking amplitude exceeds the allowable limit, the balance of the buckling amount of the sand blasting pipe joint cannot be guaranteed, and the quality of the sand blasting pipe assembly cannot be guaranteed. Therefore, for the sand blasting pipe selected for the production of sand blasting pipe assembly, it is necessary to strictly check whether the inner diameter and outer diameter of the skeleton layer meet the requirements, and the requirements for the outer diameter error can be appropriately relaxed. 2. Wall thickness error of high-pressure hose: due to the local pain of the rubber layer in the high-pressure sandblasting pipe and the influence of the overlapping width of the rubber layer of the high-pressure sandblasting pipe quality inspection center between the skeleton layers, the wall thickness error of the sandblasting pipe may be too large. If the wall thickness error exceeds the allowable range, it will affect the tightness and pull-out strength of the connector, and even cause some deflection (tilting head) of the hose assembly connector. Quality inspection of high-pressure sand blasting pipe Therefore, the wall thickness error of sand blasting pipe should be strictly controlled. Generally, the rubber hose with wall thickness error exceeding 0.5mm shall be selected stably. 3. Adhesion between each layer of high-pressure rubber hose: high-quality high-pressure sand blasting pipe shall have prominent integrity, that is, the quality inspection of high-pressure sand blasting pipe shall have high adhesion between each structural layer, and the adhesion between each adhesive layer shall become an integrity. Only in this way can we meet various technical requirements in the process of joint installation and fastening, and only in this way can we ensure the quality inspection requirements of high-pressure sand blasting pipes for sand blasting pipe assembly. Therefore, Sandblasting hose Where can I find it? It is necessary to control the adhesive force between each layer of the rubber hose not lower than that specified in the technical standard, and the rubber hose with high adhesive force shall be selected as far as possible to produce the rubber hose assembly.

wear-resisting Sandblasting hose 1. During the molding of rubber products, the cohesive force of the elastomer cannot be eliminated due to the large pressure pressing. During the molding and mold release, extremely unstable shrinkage (the shrinkage rate of rubber varies due to different rubber types) often occurs. It must take a period of time before it can be gentle and stable. Therefore, at the beginning of the design of a rubber product, no matter the formula or the mold, it is necessary to carefully calculate the matching. If not, it is easy to cause dimensional instability of the product, resulting in low product quality. 2. Rubber belongs to thermosetting elastomer, while plastic belongs to thermosetting elastomer. Due to different sulfide types, the temperature range of rubber molding and curing is quite different, even affected by climate change and indoor temperature and humidity. Therefore, the production conditions of rubber products need to be properly adjusted at any time. If not, there may be differences in product quality. 3. The rubber product is the rubber mixture made from rubber raw materials after mixing in the internal mixer as the raw material. The formula is designed according to the characteristics of the required rubber products during mixing, and the required product hardness is determined. The product is molded by the rubber plate vulcanizer. After the product is formed, flash processing shall be carried out to make the product surface smooth without burrs. 4. The aging test of rubber products belongs to the category of aging test. Rubber aging refers to the phenomenon that the performance and structure of rubber and products are changed due to the combined effect of internal and external factors in the process of processing, storage and use, thus losing their use value. Sandblasting hose Where can I find it? It is characterized by cracking, tackiness, hardening, softening, chalking, discoloration, mildew, etc. The following conditions shall be met when the ball mill uses the rubber lining plate: 1. The hardness of the ground material. The iron base alloy is similar to the rubber lining plate for materials below medium hardness, and the rubber lining plate is superior for materials above medium hardness. 2. The temperature of rubber lining plate is generally 70 ℃ - 90 ℃, and it can reach 110-130 ℃ under special circumstances. The temperature should be lower during dry grinding. 3. Feed size. Generally, the ball mill shall be more than 20-25mm; For the autogenous mill, the feeding particle size can be larger because no steel ball is added.