1. Mutual wear of rubber lining plate and steel ball of ball mill: both the rubber lining plate and steel ball of ball mill are vulnerable parts. During grinding, the steel ball and material of ball mill do throw line falling movement in the barrel Xi'an Sanding pipe It will collide with steel balls and materials and cause friction. In continuous operation, the rubber lining plate and steel ball of ball mill will be severely worn, which is directly related to the hardness of materials. The greater the hardness of the material, the faster the abrasion speed of the rubber lining plate and steel ball of the ball mill, which may cause equipment damage or even safety accidents in serious cases. In addition, it is also related to the ball of the ball mill. The size and quantity of the ball will affect the service life of the rubber lining plate of the ball mill. If the ball mill is in operation, increasing the amount of steel balls or filling steel balls with larger diameters will increase the wear of the rubber lining plate of the ball mill. 2. The heat treatment process of the rubber lining plate of the ball mill is unreasonable: the unreasonable heat treatment of the rubber lining plate of the ball mill will not only increase the wear of the lining plate, but also affect the yield strength of the lining plate, resulting in the fracture of the bolt of the ball mill under the large shear force. In the actual operation, the staff lacked the understanding of the lining plate material and the heat treatment processing of the ball mill rubber lining plate was insufficient, so the strengthening effect of the ball mill rubber lining plate was not in place and the strength was low. When impacted by steel balls and materials, Sanding pipe Where can I find it? Plastic deformation often occurs. 3. The material of the rubber lining plate of the ball mill is unreasonable: the material of the rubber lining plate of the ball mill and its heat treatment process are the key to determine the mechanical performance of the lining plate. If the material of the lining plate is not properly selected, its fatigue strength and life will be greatly reduced, which will not meet the requirements of the ball mill, or even plastic deformation or bulge will occur.

Xi'an Sanding pipe The entry threshold is low, the industry market is mixed, and small enterprises with small scale, lack of core competitiveness and low technical level can be seen everywhere. Most of these enterprises lack brand awareness, and there are many brand names and unlicensed products. It is difficult to form enterprise influence through brands, and it is more difficult to improve product added value through brands. If the metal hose wants to take the road of high-end, it must improve both inside and outside. A good brand image promotion and influence building can certainly provide a strong driving force for the development of enterprises, but the root of this driving force lies in the high quality of the metal hose products themselves. Tongfeng Metal Hose said that in the future, domestic metal hose products will focus on high precision, high efficiency, high firmness, multi-function, multi specification, multi variety standardization, serialization and generalization to show their characteristics. One of the main reasons why China's metal hoses have been in the low-end state for a long time is the lack of independent research and development of products. On the one hand, the homogenization competition is serious. In order to win consumers, metal hose enterprises have long focused on low-cost competition and low price shopping. As a result, many enterprises only focus on the production and marketing of low-end products, ignoring the upgrading and innovation of product technology. on the other hand, Sanding pipe Where can I find it? ZHUANLI's weak awareness of protection and the serious phenomenon of technology plagiarism and infringement in the industry make the technology cost invested by many enterprises more than worth the cost, which has seriously hit the enthusiasm of metal hose enterprises for innovation.

With the development of modern industry, the demand for high temperature and high pressure sandblasting hoses is growing, Sanding pipe Where can I find it? Scope of application: completely flexible conveying pipe is required to prevent the pipe from being in vibration position. It is suitable for steam, gas, air, heavy oil, petroleum, chemical industry, etc. First of all, the structure of fire sprinkler metal sandblasting hose (explosion-proof pipe) must have compulsory knowledge. Fire sprinkler metal sandblasting hose (hereinafter referred to as explosion-proof pipe) is a high-quality sandblasting hose in modern industrial pipelines. It is mainly composed of fire sprinkler metal sandblasting hose bellows, fire sprinkler metal sandblasting hose net sleeve and fire sprinkler metal sandblasting hose connector. The inner pipe is a thin-walled stainless steel fire sprinkler metal sandblasting hose corrugated pipe with spiral or circular waveform. The outer layer of the fire sprinkler metal sandblasting hose corrugated pipe is woven by stainless steel wire or steel strip according to certain parameters. The fire spraying metal sand blasting hose connector or flange at both ends of the sand blasting hose shall match with the fire spraying metal sand blasting hose connector or flange of the user's pipeline. production Sanding pipe Scope of application of fire sprinkler metal sandblasting hose (explosion-proof pipe): full flexible conveying pipe is required in vibration places to prevent pipes, which is applicable to steam, gas, air, heavy oil, petroleum, chemical industry, etc. The annular flame spraying metal sandblasting hose bellows is a special geometric pipe. The outer edges of several annular diaphragms are tangent to several concave half rings facing the center, and the inner edges are tangent to several concave half rings of the vest. Its blanks are mainly made of tubes. The fire sprinkler metal sandblasting hose bellows has the characteristics of large flexibility, good elasticity, simple manufacturing and small rigidity.

production Sanding pipe 1. During the molding of rubber products, the cohesive force of the elastomer cannot be eliminated due to the large pressure pressing. During the molding and mold release, extremely unstable shrinkage (the shrinkage rate of rubber varies due to different rubber types) often occurs. It must take a period of time before it can be gentle and stable. Therefore, at the beginning of the design of a rubber product, no matter the formula or the mold, it is necessary to carefully calculate the matching. If not, it is easy to cause dimensional instability of the product, resulting in low product quality. 2. Rubber belongs to thermosetting elastomer, while plastic belongs to thermosetting elastomer. Due to different sulfide types, the temperature range of rubber molding and curing is quite different, even affected by climate change and indoor temperature and humidity. Therefore, the production conditions of rubber products need to be properly adjusted at any time. If not, there may be differences in product quality. 3. The rubber product is the rubber mixture made from rubber raw materials after mixing in the internal mixer as the raw material. The formula is designed according to the characteristics of the required rubber products during mixing, and the required product hardness is determined. The product is molded by the rubber plate vulcanizer. After the product is formed, flash processing shall be carried out to make the product surface smooth without burrs. 4. The aging test of rubber products belongs to the category of aging test. Rubber aging refers to the phenomenon that the performance and structure of rubber and products are changed due to the combined effect of internal and external factors in the process of processing, storage and use, thus losing their use value. Sanding pipe Where can I find it? It is characterized by cracking, tackiness, hardening, softening, chalking, discoloration, mildew, etc. The following conditions shall be met when the ball mill uses the rubber lining plate: 1. The hardness of the ground material. The iron base alloy is similar to the rubber lining plate for materials below medium hardness, and the rubber lining plate is superior for materials above medium hardness. 2. The temperature of rubber lining plate is generally 70 ℃ - 90 ℃, and it can reach 110-130 ℃ under special circumstances. The temperature should be lower during dry grinding. 3. Feed size. Generally, the ball mill shall be more than 20-25mm; For the autogenous mill, the feeding particle size can be larger because no steel ball is added.

Xi'an production In places that must be crossed or may rub with the mechanical surface when working, hose clamps or springs and other protective devices should be used to prevent the outer layer of the sandblasting hose from being damaged. Sand blasting hose shall be arranged to avoid heat source as far as possible and away from the performance of engine exhaust pipe. If necessary, sleeve or protective screen can be used to prevent the hose from being heated and deteriorated. When the sand blasting hose must be bent, the bending radius should not be too small, and should be greater than 9 times the outer diameter. There should be a straight line section greater than 2 times the outer diameter of the pipe at the joint between the rubber hose and the joint. How high-quality the products and equipment we use are, it is inevitable that there will be some large and small failures in the process of using them, which will more or less have a certain impact on our work. Just like the use of sandblasting hose, there are traces of its outer adhesive seam, problems must be solved, For this, we explained the following solutions: First, the used water cloth should be used according to the original elastic edge of the water cloth when it is reused. 2： When we wrap the water cloth around the seam of the sandblasting hose, we should apply sufficient and uniform pressure to the pipe body. 3. The water cloth with different widths should be selected according to the size of the outer diameter of the wrapped sandblasting hose (for hose with an outer diameter of less than 30mm, the width of the water cloth should not exceed 90mm). The overlapping width of the water cloth should be 3/5-2/3 of the width of the water cloth.